Polymerizable diblock macromolecular monomers having a substantially uniform molecular weight distribution and their preparation

ABSTRACT

1. A POLYMERIZABLE DIBLOCK MACROMOLECULAR MONOMER OF THE FORMULA: A-B-X WHEREIN A IS A POLYMERIZED MONOALKENYL SUBSTITUTED AROMATIC HYDROCARBON, B IS A POLYMERIZED CONJUGATED DIENE, AND X IS A POLYMERIZABLE END GROUP CONTAINING EITHER A VINYL MOIETY, A VINYLENE MOIETY OR AN EPOXY MOIETY, SAID DIBLOCK MACROMOLECULAR MONOMER HAVING A MOLECULAR WEIGHT IN THE RANGE OF FROM ABOUT 5,000 TO ABOUT 150,000 AND HAVING A SUBSTANTIALLY UNIFORM MOLECULAR WEIGHT DISTRIBUTION SUCH THAT ITS RATIO OF MW/MN IS LESS THAN ABOUT 1.1, SAID DIBLOCK MACROMOLECULAR MONOMER BEING FURTHER CHARACTERIZED AS HAVING NO MORE THAN ONE VINYL MOIETY, VINYLENE MOIETY OR EPOXY MOIETY ON THE TERMINAL PORTION PER LINEAR COPOLYMER CHAIN.

' 3,842,146 Patented Oct. 15, 974

I 3,842,146 1 POLYMERIZABLE DIBLOCK MACROMOLECULAR MONOMERS HAVING A SUBSTANTIALLYUNI- FORM MOLECULAR WEIGHT DISTRIBUTION AND THEIR PREPARATION Ralph Milkovich, Naperville, and Mutong T. Chiang, Palos Heights, Ill., assignors to CPC International Inc. No Drawing. Continuation-impart of application Ser. No. 282,099, Aug. 21, 1972, which is a continuation-impart of application Ser. No. 244,205, Apr. 14, 1972, which in turn is, a continuation-in-part of application Ser. No.

117,733, Feb. 22, 1971, now abandoned. This application Apr. 2, 1973, Ser. No. 347,116

Y Int. (ll. C08f /00 US. Cl. 260879 28 Claims ABSTRACT OF THE DISCLOSURE The present invention relates to a novel composition of matter comprising: high molecular weight polymeriz': able monomers, each of said polymerizable monomers comprising at least one polymeric segment having at least about uninterrupted recurring monomeric units of at least one anionically polymerized compound, each of said polymerizable monomers terminating with no more than one polymerizable end, group containing a moiety selected fromolefinic, epoxy, or thioepoxy groups per mole of said polymerizable monomers, said polymerizable monomers denoted as having a substantially uniform molecular weight distribution such that their ratio of Hw/Hn is less than about 11, wherein fiw is the weight average molecular weight of the high molecular weight polymerizable monomers and Mn is the number average molecular weight of the high molecular weight polymerizable monomers, said polymerizable monomers being further denoted as capable of copolymerizing with a second polymerizable compound having a relatively low molecular weight to yield a chemically joined, phase separated thermoplastic graft copolymer, said copolymeriz'ation occurring through said polymerizable end group, said polymerizable end group thereby occurring as an integral part of the backbone of said chemically joined, .phase separated thermoplastic graft copolymer.

CROSS-REFERENCE TO RELATED APPLICATIONS This application is a continuation-in-part of co-pending application Ser. No. 282,099, filed Aug. 21, 1972, now US. Pat. No. 3,786,116, granted Ian. 15, 1974. Application Ser. No. 282,099 is a continuation-in-part-of.copending application Ser. No. 244,205, filed Apr. 14, 1972, which in turn is a continuation-in-part of application Ser. No. 117,733, filed February 22, 1971, saidlater patent application now abandoned.

BACKGROUND OF THE INVENTION Many poly"alpha-olefins are crystalline and have excel-' lent structural integrity; and, accordingly, have acquired increasing commercial acceptance as materials for com peting with metals and ceramicsf-As one example, poly ethylene hasbeen regarded as one of the most important polymers among the major plastics, with its production reaching about"6 billion pounds in 1970 (1.7 billion pounds of high'density linear polyethylene and 4.3 billion pounds-of low density polyethylene). 1 'Despite' the widespread use of this important plastic, its use has been limited to flexible, translucent, molded articles or flexible, clear films, due to its softness. The use of polyethylene have also been limited due to its poor adhesion to many substrates and its low heat distortion, rendering it unsuitable for manyfhigh temperature applications. I I i Attempts by prior art workers to combine the properties of polyolefins and other polymers by either chemical or mechanical means generally has resulted in a sacrifice of many of the beneficial properties of both the polyolefin and the additional polymer. For example,'graft in the art with respect to the incompatibility of polyolefins with other polymers find almost equal applicability in the case of other plastics such as the polyacrylates,

polymethacrylates, polyvinylchlorides, etc. Thus, the in compatibility of both natural and synthetic polymers becomes increasingly apparent as more and more polymers having particularly good properties for special uses have become available, and as elforts have been made to combine'pairs of these polymers for the purpose of incorporating the different, good properties of each polymer into one product. More often then not, these etforts have been unsuccessful because the resulting blends have exhibited an instability, and in many cases the desirable properties of the new polymers were completely lost. As a specific example, polyethylene is incompatible with polystyrene and a blend of the two has poorer physical (a) Statement Of The Invention The present invention relates to chemically joined, phase separated thermoplastic graft copolymers.-

(b) Description Of The Prior Art Q Polymer technology has developed to a degree of sophistication and extensive research efforts in this direc-.

tion are being undertaken to obtain improvements in:

properties than either of the homopolymers. These failures were atfirst attributed to inadequate mixing procedures, but eventually it was concluded that the failures were due simply to the inherent incompatibilities.'A1- though it is now believed that this is a correct explanation, the general nature of such incompatibility has remained somewhat unclear, even to the present. Polarity seems to be a factor, i.e., two polar polymers are apt to be more compatible than a polar polymer and a nonpolar polymer. Also, the two polymers must be structurally compositionally somewhat similar if they are to be compatible. Still further, a particular'pair of polymers-may be compatible only within a certain range of range they' are incompatible. v v

Despite the general acceptance of the fact of incomr elativ e' proportions of the two polymers; outside that patibility of polymer pairs, there is much interest in' devising means whereby the advantageous properties of combinations of polymers may be combined into one product.

One way in which this objective has been sought involves the preparation of block or graft copolymers. In this way, two different polymeric segments, normally incompatible with one another, are joined together chemically to give a sort of forced compatibility. In such a copolymer, each polymer segment continues to manifest its independent polymer properties. Thus, the block or graft copolymer in many instances possesses a combination of properties not normally found in a homopolymer or a random copolymer.

Recently U.S. Pat. No. 3,235,626 to Waack, assigned to Dow Chemical Company, described a method for preparing graft copolymers of controlled branch configuration. It is described that the graft copolymers are prepared by first preparing a prepolymer by reacting a vinyl metal compound with an olefinic monomer to obtain a vinyl terminated prepolymer. After protonation and catalyst removal, the prepolymer is dissolved in an inert solvent with a polymerization catalyst and is thereafter reacted with either a different polymer having a reactive vinyl group or a different vinyl monomer under freeradical conditions.

The current limitations on the preparation of these copolymers are mechanistic. Thus, there is no means for controlling the spacing of the sidechains along the backbone chain and the possibility of the sidechains having irregular sizes. Due to the mechanistic limitations of the prior art methods, i.e., the use of an alpha-olefin terminated prepolymer with acrylonitrile or an acrylate monomer, complicated mixtures of free homopolymers results.

In view of the above considerations, it would be highly desirable to devise a means for preparing graft copolymers wherein the production of complicated mixtures of free homopolymers is minimized and the beneficial properties of the sidechain and backbone polymer are combined in one product.

Moreover, it is recognized and doucmented in the literature, such as R. Waack et al., Polymer, Vol. 2, pp. 365- 366 (1961), and R. Waack et al., J. Org. Chem., Vol. 32, pp. 33953399 (1967), that vinyl lithium is one of the slowest anionic polymerization initiators. The slow initiator characteristic of vinyl lithium when used to polymerize styrene produces a polymer having a broad molecular weight distribution due to the ratio of the overall rate of propagation of the styryl anion to that of the vinyl lithium initiation. In other words, the molecular weight distribution of the polymer produced will be determined by the effective reactivity of the initiator compared with that of the propagating anionic polymer species, i.e., vinyl lithium initiator reactivity compared to the styryl anion. Accordingly, following the practice of US. Pat. No. 3,235,626, a graft copolymer having sidechains of uniform molecular weight cannot be prepared.

US. Pat. Nos. 3,390,206 and 3,514,500 describe processes for terminating free-radical and ionic polymerized polymers with functional groups which are described as capable of copolymerizing with polymerizable monomers. The functionally terminated prepolymers described by rhese patents also would be expected to have a broad molecular weight distribution and, therefore, would not be capable of producing a chemically joined, phase separated thermoplastic graft copolymer.

SUMMARY OF THE INVENTION The present invention relates to thermoplastic graft copolymers comprised of copolymeric backbones containing a plurality of uninterrupted'repeating units of the back.- boue polymer and at least one integrally copolymerized moiety per backbone polymer chain having chemically bonded thereto a substantially linear polymer which forms a copolymerized sidechain to the backbone, wherein each of the polymeric sidechains has substantially the .same molecular weight and each polymeric sidechain is chemically bonded to only one backbone polymer.

The graft copolymers of the present invention assume a T type structure when only one sidechain is copolymerized into the copolymeric backbone. However, when more than one sidechain is copolymerized into the backbone polymer, the graft copolymer may be characterized as having a comb-type structure illustrated in the following manner:

l l I 8 a a I l 8 3 a wherein represents a substantially linear, uniform molecular weight polymer or copolymer having a sufiicient molecular Weight such that the physical properties of at least one of the substantially linear polymers are manifest; b represents a reacted and polymerized end group chemically bonded to the sidechain, a, which is integrally polymerized into the backbone polymer, and c is the backbone polymer having uninterrupted segments of sufficient molecular weight such that the physical properties of the polymer are manifest.

The backbone of the graft copolymers of the present invention preferably contains at least about 20 uninterrupted recurring monomeric units in each segment. It has been found that this condition provides the graft copolymer the properties of the polymer. In other words, the presence' of segments containing at least about 20 uninterrupted recurring monomeric units provides the graft copolymers with the physical properties attributed to this polymer, such as crystalline melting point (Tm) and structural integrity.

The backbone polymeric segments of the chemically joined, phase separated thermoplastic graft copolymers of the present invention are derived from copolymerizable monomers, preferably the low molecular weight monomers. These copolymerizable monomers include polycarboxylic acids. their anhydrides and amides, polyisocyanates, organic epoxides, including the thioepoxides, ureaformaldehydes, siloxanes, and ethylenically unsaturated monomers. A particularly preferred group of copolymerizable monomers includes the ethylenically-unsaturated monomers, especially the monomeric vinylidene type compounds, i.e., monomers containing at least one vinylidene CH =(iJ group. The vinyl type compounds represented by the formula wherein a hydrogen is attached to one of the free valences of the vinylidene group are contemplated as falling Within the generic scope of the vinylidene compounds referred to hereinabove.

The backbone polymers of the present invention are also comprised of polyolefins which include polymers of alpha-olefins of the formula: CH =CHR wherein R is either hydrogen, or an alkyl or aryl radical containing 1 to about 16 carbon atoms, and include ethylene, propylene, butene-l, pentene-l, hexene-l, styrene, etc.; copolymers of alpha-olefins including the ethylene-propylene copolymers; and polymers of polymerizable dienes including butadiene, isoprene, etc.

The copolymerizable monomers useful in the practice of the present invention are not limited by the exemplary classes of compounds mentioned above. The only limitation on the particular monomers to be employed is their capability to copolymerize with the polymerizable end groups of the sidechain prepolymer under free-radical, ionic, condensation, or coordination (Ziegler or Ziegler-Natta catalysis) polymerization reactions. As it will be seen from the description of macromolecular mono-. mers, described hereinbelow, the choice of polymerizable end groups includes any polymerizable compound commercially available. Accordingly, the choice of respec tive polymerizable end group and copolymerizable monomer can be chosen, based upon relative reactivity "ratios under the respective copolymerization reaction conditions suitable for copolymerization reaction. 'For example, a'lpha-olefins copolymerize with one another'using'Ziegler catalysts, and a'crylates copolymerize with vinyl chloride, acrylo-nitrile and other alkylacrylates. Accordingly, an alpha-olefin terminated macromolecular monomer copolymerizes with ethylene and 'alpha-olefins usinga Ziegler catalyst and an acrylate or methacrylate terminated macromolecular monomer copolymerizes with vinyl chloride, acrylonitrile, acrylates and methacrylates under free-radical conditions in a manner governed by the respective reactivity ratios for the comonomers. As will be explained hereinafter, the excellent combination of beneficial properties possessed by the graft copolymers of the present invention are attributed to the large segments of uninterrupted copolymeric backbones and the integrally copolymerized linear side-chains of controlled molecular weight and narrow molecular weight distribution;

The term linear, referred to hereinabove, is being used in its conventional sense, to pertain to a polymeric backbone that is free from cross-linking.

, The sidechain polymers having substantially uniform molecular weight are comprised of substantially linear polymers and copolymers produced by anionic polymerization of any anionically polymerizable monomer, as will be described hereinafter. Preferably, the sidechain polymer will be different than the backbone polymer.

It is preferred that at least one segment of the sidechain polymer of the graft copolymers of the present invention have a molecular weight suflicient to manifest the beneficial properties of the respective polymer. In other words, physical properties of the sidechain polymer such as the glass transition temperature (Tg) will be manifest. Generally, as known in the art, the average molecularweight of the segment of the polymeric sidechains necessary to'establish the physical properties of the polymer will be from about 5,000 to about 50,000.

' In light of the unusual and improved physical properties possessed by the thermoplastic graft copolymers of the present invention, it is believed that monofunctionally bonded polymeric 'sidechains having substantially uniform molecular weight form what is known as glassy domains representing areas of mutual solubility of the respective sidechain polymers from separate backbone copolymers.

STATEMENT OF THE INVENTION Briefly, the chemically joined, phase separated thermoplastic graft copolymers of the present invention are prepared by first preparing the sidechains in the form of monofunctional living polymers of substantially uniform molecular weight. The living polymers are thereafter terminated,'as by reaction with a halogen-containing compound that also contains a reactive polymerizable group, suchas, for example, a polymerizable olefinic' or epoxy group, or a compound which contains a reactive site to a carbanion of the living polymer and a polymerizable moiety which does not preferentially react with the carbanion, e.g., maleic anhydride. The monofunctional terminated living polymer chains are then polymerized, together with the backbonemonomer, to form a chemically joined, phase separated thermoplastic graft copolymer wherein the polymeric sidechains are integrally polym erized into the backbone polymer.

DESCRIPTION OF PREFERRED EMBODIMENTS The chemically joined, phase separated thermoplastic graft copolymers derived from ethylenically unsaturated 6 monomers as the backbone comonomer generally correspond to the' following structural formula;

, i l LL L .12

wherein R is alkyl or aryl), nitrile (i.e., CEN), amide (i.e.,

wherein R and R" are either hydrogen, alkyl or aryl radicals), amine (i.e.,

wherein R and R are either hydrogen, alkyl or aryl radicals), isocyanate, halogen (i.e., F, Cl, Br or I) and ether (i.e., -OR, wherein R is either alkyl or aryl radicals); X and X may be the same or different. However, in the case where X is an ester, X should be a functional group such as ester, halogen, nitrile, etc.,- as explained hereinabove with respectto the respective reactivity ratios of the comonomers used to prepare the graft copolymers; Y is a substantially linear polymer or copolymer wherein at least one segment of the polymer has a sufficient molecular weight to manifest the properties of the respective polymer, i.e., a molecular weight of I from about 5,000 to about 150,000, very suitable polymers having a. molecular weight in the range of from about 5,000 ,to about 50,000, preferably a molecular weight of from about 35,000, more preferably 12,000 to about 25,000; the symbols a, b and c are positive integers, with the proviso that a and b are each a value such that the physical properties of the uninterrupted segments in the backbone, e.'g., Tm, are manifest, preferably at least about 20; and the symbol 0 is at least one, but preferably greater than one, e.g., a value such that the molecular weight of the graft copolymer will be up to about 2, 0.

The formation of the graft copolymers of the present invention may be better understood by reference to'the following reactions illustrated by the equations set forth below wherein the invention is illustrated in terms 'of polystyrene sidechains; and polyethylene backbones. It can be seen from these equations that the first reactions involve the preparation of living polymers ofpolystyrene. The living polymers are thereafter reacted with a molar equivalent of allyl chloride, wherein'the -reaction takes place at the" carbon-chloride bond, rather than at the carbon-carbon double bond. The vinyl terminated polystyrene, referred to herein as the alpha-olefin terminated macromolecular monomer, is then copolymerized with ethylene to produce a graft copolymer polyethylene, whereby the-vinyl moiety of the polystyrene is integrally polymerized into the linear polyethylene backbone.

Alternatively, the living polymer can be reacted with an epoxide such as, for example, ethylene oxide, to produce an alkoxide ion which can then be reacted with the halogen-containing olefin, i.e., allyl chloride, to produce an alpha-olefin terminated macromolecular monomer. This, in essence, places the terminal alpha-olefin farther away from the aromatic ring of the polystyrene and therefore reduces any steric hindering influence that might be exerted by the aromatic ring.

FORMATION OF THE GRAFT COPOLYMER OF ALPHA- OLEFIN TERMINATED POLYSTYRENE SIDECHAIN AND POLYETHYLENE BACKBONE (11-1) crn=c n1 Termination with CH =CHCHC1 Active End Group:

Craft Copolymerlzation: lxCHFCIh Polymerization Catalyst CHT'CHl CHI C H CHa-CHr\:L1- L- Ja 6H L Jr;

CH3 CH2(CH3) CH CHr C H In the equations above, the symbols a, b, c, n and X are positive integers wherein a and b are at least about 20, n has a value of from about 50 to about 500, and x has a value corresponding approximately to the sum of a and b.

PREPARATION OF THE LIVING POLYMERS The sidechains of the chemically joined, phase separated graft copolymers, above, are preferably prepared by the anionic polymerization of a polymerizable monomer or combination of monomers. In most instances, such monomers are those having an olefinic group, such as the vinyl containing compounds, although the olefinic containing monomers may be used in combination with epoxy or thioepoxy containing compounds. The living polymers are conveniently prepared by contacting the monomer with an alkali metal hydrocarbon or alkoxide salts 8 in the presence of an inert organic diluent which does not participate in or interfere with the polymerization reaction.

Those monomers susceptible to anionic polymerization are well-known and the present invention contemplates the use of all anionically polymerizable monomers. Nonlimiting illustrative species include vinyl aromatic compounds, such as styrene, alpha-methylstyrene, vinyl toluene and its isomers; vinyl unsaturated amides such as acrylamide, methacrylamide, N,N-dilower alkyl acrylamides, e.g., N,N-dimethylacrylamide; acenaphthalene; 9- acrylcarbazole; acrylonitrile and methacrylonitrile; organic isocyanates including lower alkyl, phenyl, lower alkyl phenyl and halophenyl isocyanates, organic diiso cyanates including lower alkylene, phenylene and tolylene diisocyanates; lower alkyl and allyl acrylates and methacrylates, including methyl, t-butyl acrylates and methacrylates; lower olefins, such as ethylene, propylene, butylene, isobutylene, pentene, hexene, etc.; vinyl esters of aliphatic carboxylic acids such as vinyl acetate, vinyl propionate, vinyl octoate, vinyl oleate, vinyl stearate, vinyl benzoate; vinyl lower alkyl ethers; vinyl pyridines, vinyl pyrrolidones; dienes including isoprene and butadiene. The term lower is used above to denote organic groups containing eight or fewer carbon atoms. The preferred olefinic containing monomers are conjugated dienes containing 4 to 12 carbon atoms per molecule and the vinyl-substituted aromatic hydrocarbons containing up to about 12 carbon atoms.

Many other monomers suitable for the preparation of the sidechains by anionic polymerization are those disclosed in Macromolecular Reviews: Volume 2, pages 74- 83, Interscience Publishers, Inc. (1967), entitled Monomers Polymerized by Anionic Initiators, the disclosure of which is incorporated herein by reference.

The initiators for these anionic polymerizations are any alkali metal hydrocarbons and alkoxide salts which produce a monofunctional living polymer, i.e., only one end of the polymer contains a reactive anion. Those catalysts found suitable include the hydrocarbons of lithium, sodium or potassium as represented by the formula RMe wherein Me is an alkali metal such as sodium, lithium or potassium and R represents a hydrocarbon radical, for example, an alkali radical containing up to about 20 carbon atoms or more, and preferably up to about eight carbon atoms, an aryl radical, an alkaryl radical or an aralkyl radical. Illustrative alkali metal hydrocarbons include ethyl sodium, n-propyl sodium, n-butyl potassium, noctyl potassium, phenyl sodium, ethyl lithium, sec-butyl lithium, t-butyl lithium and 2-ethylhexyl lithium. Secbutyl lithium is the preferred initiator because it has a fast initiation which is important in preparing polymers of narrow molecular Weight distribution.- It is preferred to employ the alkali metal salts of tertiary alcohols, such as potassium t-butyl alkoxylate, when polymerizing monomers having a nitrile or carbonyl functional group.

The alkali metal hydrocarbons and alkoxylates are either available commercially or may be prepared by known methods, such as by the reaction of a halohydrocarbon, halobenzene or alcohol and the appropriate alkali metal.

An inert solvent generally is used to facilitate heat transfer and adequate mixing of initiator and monomer. Hydrocarbons and ethers are the preferred solvents. Solvents useful in the anionic polymerization process include the aromatic hydrocarbons such as benzene, toluene, xylene, ethylbenzene, t-butylbenzene, etc. Also suitable are the saturated aliphatic and cycloaliphatic hydrocarbons such as n-hexane, n-heptane, n-octane, cyclohexane and the like. In addition, aliphatic and cyclic ether solvents can be used, for example, dimethyl ether, diethyl ether, dibutyl ether, tetrahydrofuran, dioxane, anisole, tetrahydropyran, diglyme, glyme, etc. The rates of polymerization are faster in the ether solvents than in the hydrocarbon solvents, and small amounts of ether in the hydrocarbon solvent increase the rates of polymerization.

The amount of initiator is an important factor in anionic polymerization because it determines the molecular weight of the living polymer. If a small proportion of initiator is used, with respect to the amount of monomer, the molecular weight of the living polymer will be larger than if a large proportion of initiator is used. Generally, it is advisable to add initiator dropwise to' the monomer (when that is the selected order of addition) until the persistence of the characteristic color of the organic anion, then add the calculated amount of initiator for the molecular weight desired. The preliminary dropwise addition serves todestroy contaminants and thus permits better control of the polymerization.

To prepare a polymer ofv narrow molecular weight distribution, .it is generally preferred tointroduce allof the reactive species into the system at the same time. By this technique, polymer growth. by' consecutive addition of monomer takes place at the same .rate toan active terminal group, without chaintransfer. or. termination reaction. When this is accomplished, the molecular weight of the polymer is' controlled by the ratio of monomer to initiatonas seen from the following representation:

Molecular weight of living polymer Moles of monomer .Moles of initiator Xmoleculal: .welghyof monomer 4 I it can be seen from the above formula, high concentrations ,of initiator leads to the formation of low molecular weight polymers, whereas, low concentrations of' initiator leads to the production of high molecular weight "polymers. v

The concentration of the monomer charged to the 'react'ieii vessel can vary widely, and is limited by the ability'of the reaction equipment to dissipate the heat of polymerization and'to properly mix the resulting viscous solutions of the living polymer. Concentrations of mono- 'mer as high as 50% by Weight or h'igher basedon the "weight of the reaction mixture can be used. However, the preferred monomer concentration is from about 5% 'to'about 25% in order to achieve adequate mixing. 1

As can be seen from the formula above and the foregoinglimitations on the concentration'of the monomer, the "initiator concentration is criticahfbutmay belva'rie'd according to the desired molecular weight of the living polymer and the relative concentration of the monomer.

"Generally, the initiator concentration can range from about 0.001 to about 0.1 mole of active alkali metal'per mole of monomer, or higher. Preferably, the' concentration of the initiator will befrom about 0.01 to about0.004

mole of active alkali metal per mole of r'nonomerl The temperature of the polymerization" will 'dependon the monomer. Generally, the reaction can be carried out at temperatures ranging from about 100'C. up to about 100 C. When using aliphatic and hydrocarbon diluents, the'preferred temperature range is from about C. to

about 100 C. With ethers as the solvent, the preferred temperature range is from about 100 C. to about-100 C. The polymerization of the styrene is generally carried out at slightly above room temperature; the "polymerization of alpha-methylstyrene preferably is carried' out at lower temperatures, e.g., 80 C. 3

The preparation of the living polymer can becarried out by adding a solution of the alkali metal hydrocarbon initiator in an inert organic solvent to a mixture of 'inono- 'rea'ctive ingredients together rapidly to-insure theformation of a uniform molecular weight distribution of the polymer.

The anionic polymerization must be carried out under carefully controlled conditions, so as to exclude substances which destroy'the catalytic effect of the catalyst or initiator. For example, such impurities as water, oxygen, carbon monoxide, carbon dioxide, and the like. Thus, the polymerizations are generally carried out in dry equipment, using anhydrous reactants, and under an inert gas atmosphere, such as nitrogen, helium, argon, methane, and the like.

The above-described living polymers are susceptible to further reactions including further polymerization. Thus, if additional monomer, such as styrene, is added to the living polymer, the polymerization is renewed and the chain grows until no more monomeric styrene remains. Alternatively, if another different anionically polymerizable monomer is added, such as butadiene or ethylene oxide, the above-described living polymer initiates the polymerization of the butadiene or ethylene oxide and the ultimate living polymer which results consists of a polystyrene segment and a polybutadiene or polyoxyethylene segment.

A poly(styrene-ethylene) block copolymer can be prepared by contacting livingpolystyrene with ethylene in the presence of a compound of a transition metal of Group VVIII in the Periodic Table, e.g., titanium tetrachloride. This technique is also applicable to the alpha-olefins, such as propylene. The resulting copolymer is still a living polymer and can be terminated by the methods in accordance to the practice of the present invention.

As noted above, the living polymers employed in the present invention are characterized by relatively uniform molecular weight, i.e., the distribution of -molecular weights of the mixture of living polymers produced is quite narrow. This is in marked contrast to the typical polymer, where the molecular weight distribution is quite broad. The difference in molecular Weight distribution is particularly evident from an analysis of the gel permeation chromatogram of commercial polystyrene (Dow 666u) prepared' by free-radical polymerization ;and polystyrene produced by the anionic polymerization process utilized in accordance withthe practice of the present invention.

PRODUCTION OF THE MACROMOLECULAR MONOMERS BY TERMINATION OF THE LIVING POLYMERS The living ,polymers herein are terminated by reaction with a halogen containing compound which also contains a polymerizable moiety, such as'an olefinic group or an epoxy or thioepoxy group. Suitable halogen-containing terminating agents include: the vinyl haloalkyl ethers wherein the alkyl groups contain six or fewer carbon atoms such as methyl, ethyl, propyl, butyl, isobutyl, secbutyl, amyl or hexyl; vinyl esters of haloalkanoic acids wherein the alkanoic acid contains six or. fewer carbon atoms, such as acetic, propanoic, butyric, pentanoic, or hexanoic acidtolefinic halides having six or fewer carbon atoms such as vinyl halide, allylhalide,'methallyl halide, 6-halo-l-hexene, etc.; halides? of dienes such as Z-halomethyl-1,3-butadiene, epihalohydrins, acrylyl and methacrylyl halides, haloalkylmaleic anhydrides; haloalkylmaleatc esters; vinyl haloalkylsilanes; vinyl haloaryls; and vinyl haloalkaryls, such as vinylbenzyl chloride (VBC); haloalkyl norbornenes, such as bromomethyl norbornene, bromonorbornane, and epoxy compounds such as ethylene or propylene oxide. The 'halo group may be chloro, fluoro, bromo, or iodo; preferably, it is chloro. Anhydrides of compounds having an olefinicgroup or anepoxy or thioepoxy groupimay also be employedfsuch as maleic anhydride, acrylic or methacrylic anhydride. The following 1 1 i I 12 equations illustrate the typical termination reactions in (i) R1 accordance with the practice of the present invention:

,/ L l tLin 1'1 i R1 R CH Terminating Agents: l i I R-CH2C-OHzCCH2-C (a) XR -OC=CH L J H II"4 10 R2 n R: CH,

(10) O In the above equations, R, R R R and R are each Il selected from the group consisting of hydrogen and lower 2 alkyl, and aryl radicals. Preferably, R will be lower alkyl, XR C=CH 5 such as sec-butyl; R will be either hydrogen or methyl; R will be phenyl; R will be hydrogen or lower alkylene radical; and R will be either hydrogen or lower alkyl radi- 0 cal. The symbol n is a positive integer such that the properties of the polymer are manifest, i.e., a value such that the polymer will have a molecular weight in the range of (e) from about 5,000 to about 50,000, preferably a molecular weight in the range of from about 10,000 to about 35,000, more preferably a molecular weight in the range of from about 12,000 to about 25,000. (r) XR=cCO Termination of the living polymer by any of the above I types of terminating agents is accomplished simply by R 0 6 adding the terminating agent to the solution of living polymer at the temperature at which the living polymer is (g) X .R3 C COQR8 prepared. Reaction is immediate and the yield is theoretical. A slight molar excess of the terminating agent, with respect to the amount of catalyst, may be used although (h) X-R=-siRRo=GHz the reaction proceeds on a mole-for-mole basis.

The termination may be conducted in any suitable inert l R solvent. Generally, it is advisable to utilize the same sol- (i) vent system employed in the preparation of the living 2 polymer. A preferred embodiment of the invention comprises conducting the termination reaction in a hydrocarbon solvent rather than the polar ether type solvents such X CH2 40 as tetrahydrofuran. It has been found that the hydrocar- CH2=C C=CH bon solvents such as the aromatic hydrocarbons, saturated I" f? aliphatic and cycloaliphatic hydrocarbons cause several R-OHzC-CHz-CR*OC=CH2 difierences in the reaction conditions and the resulting L l product. For example, the termination reaction can be conducted at higher temperatures with hydrocarbon sol- (b) I" vents as opposed to the ether solvents.

R CHZ C CH2 C RB O OCZGHQ In some instances, because of the nature of the living L R: J R2 R polymer and the monomer from which it is prepared, or because of the nature of the terminating agent, certain (c) R 'l R1 5 deleterious side reactions occur which result in an impure product. For example, the carbanion of some living poly- L J mers have a tendency to react With functional groups or R2 R2 R4 any active hydrogens of the terminating agent. Thus, for (d) I- v 1'11] l example, acrylyl or ngethacrylyfl 1chloride whilfe tgieyhtlict as terminating agents ecanse o t e presence 0 e c o- 1| rine atom in their structure, they also provide a carbonyl n group in the terminated polymer chain, and this carbonyl (e) R1 0 group may provide a center for attack by a second highly I II reactive living polymer. The resulting polymer either has twice the expected molecular weight or contains some i. RLL R2 chlorine, indicating that some of the living polymer has (I) R R been terminated by reaction with a second living polymer or with one of the active hydrocarbons of the acrylyl or Q methacrylyl chloride.

L RLL R" 0 It has been discovered that one means for overcoming 6 the foregoing problem is to render the reactive carbanion less susceptible to reaction with the functional groups or (g) I- R1 R any active hydrogens of a terminating agent. A preferred S method to render the living polymer less susceptible to the L l l I R4 g C 0 adverse reaction is to cap the highly reactive living polymer with a lesser reactive reactant. Examples of some I- 1- 1 preferred capping agents include the lower alkylene oxides, i.e., one having eight or fewer carbon atoms such L J as ethylene and propylene oxide; diphenyl ethylene, etc. It n R" The capping reaction yields a product which still is a 13- living polymer, but yields a purer product when subsequently reacted with a terminating agent containing a functional group or active hydrogen.

It has been found that diphenyl ethylene is an excellent capping agent when terminating agents such as, for example, vinyl chloroalkanoates are employed.

: A particularly preferred capping agent'is a'n alkylene oxide} such as 'e'thylenebxide. It reacts with the living polymer, with the destruction of its oxirane ring. The following is a typical illustration of the capping reaction which shows the reaction of ethylene oxide as a capping agent with a living'polymer prepared by the polymerization of styrene with sec-butyl lithium as the initiator:

The capping reaction iscarried out quite simply, as in the case of the terminating reaction, by adding the capping reactant to the living polymer at polymerization temperatures. The reaction occurs immediately. As in the case of the termination reaction, a slight molar excess of the capping reactant with respect to the amount of initiator may be used. The reaction "occurs on a mole-for-mole basis. a

It will be understood that when a large molar excess of alkylene' oxide is reacted with the living polymer, a living polymer having two polymeric blocks is produced. A typical example with polystyrene segments and polyoxyalkyl ene segments is illustrated as follows:

wherein at is a positive integer. Either of the above-described ethylene oxide capped polyrr'iers can be conveniently terminated with a compound. containing arnoiety reactiye With the anion of the cappedpolymer and a polymerizable end group, including the following typical compounds: acrylyl chloride, methacrylyl" chloride, vinyl-'2 chloroethyl ether, vinyl chloroacetatq chloro'rnethylmaleic anhydride and its esters,,'. maleic anhydride (yields .half ester of maleic acid follpwingprotonation with. water), allyl and methallyl chloride and vinylbenzyl chloride. 7

The. reaction came above-described capped living polymersjwith either acrylyl or methacrylyl chloride can be represented-by the follo'wing'reaction: Y

wherein n is a positive integer of about at least 50, x is either 0 or a positive integer and R is either hydrogen or methyl.

When an epihalohydrin is used as the terminating reagent, the resulting polymer contains a terminal epoxy group. This terminal epoxy may be used as the polymerizable group itself, such as in the preparation of a polyisobutylene or a polypropylene oxide backbone graft copolymer or may be converted to various other useful polymerizable end groups by any one of several known reactions.

As one embodiment of the invention, the terminated polymer containing an epoxy or thioepoxy end group may be reacted with a polymerizable carboxylic acid halide, such as acrylic, methacrylic, or maleic acid halide, to produce a beta-hydroxyalkyl acrylate, methacrylate or maleate ester as the polymerizable terminal moiety of the substantially uniform molecular weight polymer. These same polymerizable esters may be prepared from the terminal epoxy polymer by first converting the epoxy group to the corresponding glycol by warming the polymer with aqueous sodium hydroxide, followed by conventional esterification of the glycol end group with the appropriate polymerizable carboxylic acid, or acid halide.

The resulting glycol obtained by the aqueous hydrolysis of the epoxy group in the presence of a base may be converted to a copolymer by reaction with a high molecular weight dicarboxylic acid Which may be prepared, e.g., by the polymerization of a glycol or diamine with a molar excess of phthalic anhydride, maleic anhydride, succinic anhydride, or the like. These reactions can be modified to obtain a polystyrene block and a polyamide block (Nylon). The glycol terminated polymer may also be reacted with a diisocyanate to form a polyurethane. The diisocyanate may be e.g., the reaction product of a polyethylene glycol having an average molecular Weight of 400 with a molar excess of phenylene dlisocyanate.

In another embodiment of the invention, an organic epoxide is copolymerized with a terminated polymer containing an epoxy or thioepoxy end group. The graft copolymer which results is characterized by a backbone having uninterrupted segments of at least about 20, and preferably atleast about 30, recurring units of the organic epoxide. Preferred organic epoxides include ethylene oxide, propylene oxide, butylene oxide, hexylene oxide, cyclohexene epoxide and styrene oxide, i.e., those having 8 or fewer carbon atoms.

When a haloalkylmaleic anhydride or haloalkylmaleate ester is used as the terminating agent, the resulting terminal groups can be converted by hydrolysis to carboxyl groups. The resulting dicarboxylic polymer may be copolymerized with glycols or diamines to form polyesters and polyamides having a graft copolymer structure.

If it is desired to isolate and further purify the macromolecular monomer from the solvent from which it was prepared, any of the known techniques used by those skilled in the art in recovering polymeric materials may be used. These techniques include: (1) solvent-non-solvent precipitation; (2) evaporation of solvent in an aque-' ous media; and (3) evaporation of solvent, such as by vacuum roll drying, spray drying, freeze drying; and (4) steam jet coagulation. 1

The isolation and recovery of the macromolecular monomer is not a critical feature of the invention. -In fact, the macromolecular monomer need not be recovered at all. Stated otherwise, the macromolecular monomer, once formed, an be charged with the suitable monomer and polymerization catalyst to conduct the graft copolymerization in the same system as the macromolecular monomer was prepared, providing the solvent and materials in the macromolecular monomer preparation reactor do not poison the catalyst or act in a deleterious manner to the graft copolymerization process. Thus, a judicious selection of the solvent and purification of the reactor system in the preparation of the macromolecular monomer can ultimately result in a large savings in the production of the graft copolymers of the present invention.

As pointed out above, the macromolecular monomers, which ultimately become the sidechains of the graft copolymers by being integrally polymerized into the backbone polymer, must have a narrow molecular weight distribution. Methods for determining the molecular weight distribution of polymers such as the macromolecular monomers are known in the art. Using these known methods, the weight average molecular weight (MW) and the number average molecular weight (fin) can be ascertained, and the molecular weight distribution (17w/ H12) for the macromolecular monomer can be determined. The macromolecular monomers must have nearly a Poisson molecular weight distribution or be virtually monodisperse in order to have the highest degree of functionality. Preferably, the ratio of Hw/fin of the novel macromolecular monomers will be less than about 1.1. The macromolecular monomers of the present invention possess the aforementioned narrow molecular weight distribution and purity due to the method of their preparation, described hereinabove. Thus, it is important that the sequence of steps in preparing the macromolecular monomers be adhered to in order to produce the optimum results in beneficial properties in the graft copolymers.

GRAFT COPOLYMERIZATION Prior to the invention herein, graft copolymers were prepared by synthesizing a linear backbone, then grafting onto this backbone, growing polymeric or preformed polymeric chains. These methods generally require elaborate equipment and produce a mixture of products having inferior properties unless further purified. Because of the additional processing conditions and the use of special equipment, these processes are not economically feasible.

Although some of the prior art graft copolymers, such as those described in US. Pat. Nos. 3,627,837, 3,634,548 and 3,644,584 and British Pat. Nos. 87,656 and 1,144,151 resemble the graft copolymers of the present invention. Generally, the present graft copolymers are different compositions, not only because they are prepared by significantly different processes, but because the pendant polymeric chains of the graft copolymers of this invention are of relatively uniform, minimum length, and are each an integral part of the backbone. Furthermore, the backbone of the graft copolymers of the present invention contain polymeric segments of certain minimum length. Thus, the present graft copolymers differ structurally because the macromolecular monomer is interposed between polymeric segments of the backbone polymer, rather than being merely attached to the backbone polymer in a random manner. These characteristics contribute materially to the advantageous properties which inhere in these novel graft copolymers.

The graft copolymers of the present invention are prepared by first synthesizing the pendant polymeric chains (the polymerizable terminated living polymers) then copolymerizing the terminal portions of the polymeric chains with the second monomer during the formation of the backbone polymer.

In accordance with the .practice of the present invention, the substantially pure macromolecular monomers of high controlled molecular weight and molecular Weight distribution have an appropriate reactive end group suitable for any mechanism of copolymerization, e.g., freeradical, cationic, anionic, Ziegler catalysis, and condensation. Thus, the reactive end group is selected for easycopolymerization with low cost monomers by conventional meansand within existing polymerization equipment.

The copolymerization with the macromolecular monomers and the second reactive monomer is a graft-like structure where the pendant chain is a polymer whose molecular weight and distribution are predetermined by independent synthesis. The distribution of the sidechain polymer along the backbone is controlled by the reactivity ratios of the comonomers.

Since the reactive end group of the macromolecular monomer is copolymerized with the second monomer, it is an integral part of the backbone polymer. Thus, the polymerizable end group of the macromolecular monomer is interposed between large segments of the backbone polymer. 7 i

The present invention provides a means for controlling the structure of the graft copolymer. More specifically, the control of the structure of the graft copolymer can be accomplished by any one or all of the following means: (1) by determining the reactivity ratio of the macromolecular monomer and a second monomer during the copolymerization reaction, a pure graft polymer free from contamination by homopolymers can be prepared; (2) by controlling the monomer addition rates during the copolymerization of a macromolecular monomer and a second monomer, the distance between the sidechains in the polymer structure can be controlled; and (3) the size of the graft chain can be predetermined and controlled in the anionic polymerization step of the preparation of the macromolecular monomer.

It will be apparent to those skilled in the art that by the proper selection of terminating agents, all mechanisms of copolymerization may be employed in preparing the controlled phase separated graft copolymers.

As alluded to hereinabove, the chemically joined, phase separated graft copolymers of the present invention are preferably copolymerized with any ethylenically-unsaturated monomer including the vinylidene type compounds containing at least one vinylidene group and preferably the vinyl-type compounds containing the characteristic CH =CH- group wherein hydrogen is attached to one of the free valences of the vinylidene group. The copolymerization, as pointed out above, is only dependent upon the relative reactivity ratios of the terminal group and the comonomer.

Examples of some of the preferred ethylenically-unsaturated compounds used as the comonomers include the acrylic acids, their esters, amides and nitriles including acrylic acid, methacrylic acid,'the alkyl esters 'of'acrylic and methacrylic acid, acrylonitrile, methacrylonitrile, acrylamide, methacrylamide, N,N-"dimethacrylamide (NNDMA); the vinyl halides such as vinyl chloride, and vinylidene chloride; the vinyl cyanides such as vinylidene cyanide (1,1-dicyanoethylene); the vinyl esters of the fatty acids such as vinyl acetate, vinyl propionate and vinyl chloroacetate, etc.; and the vinylidene containing dica'rboxylic anhydrides, acids and esters, fumaric acid and esters, maleic anhydrides, acids and esters'thereof.

A particularly important class of vinylidene type'c'ompounds useful as comonomers' with the alpha-olefin and styrene terminated macromolecular monomers include the vinyl olefinic hydrocarbons, such as" ethylene, propylene, l-butene, isobutylene, l-pentene, l-hexene, styrene, -3- methyl l butene, 4-methyl-1-hexene'and cyclohe'xene. Also, there may be used as'the-comonomers thepolyolefinic materials containing at least 'one'vinylidene group such as the butadiene-l,3 hydrocarbons including 'butadiene, isoprene, piperylene and other conjugated dienes, as well as other conjugated and non-conjugated polyolefinic monomers including divinyl-benzene, the diacrylate type 'nated with epichlorohydrin will contain an epoxy terminal mers of the invention copolymerize with commercial vinyl I izations with other monomers (M are described only 'isoprene.

In addition to the hereinabove described ethylenicallyunsaturated comonomers useful in the practice of the invention, there are included the comonomers capable of copolymerizing by condensation or step-reaction polymerization conditions with the polymerizable macromolecular monomers of the invention. In this connection, the polymerizable macromolecular monomers will contain the appropriate terminal groups necessary to facilitate the condensation reaction. For example, living polymers termigroup which converts to a living polymers terminated with halomaleic anhydride or -halomaleate ester may be converted to terminal carboxyl groups by conventional hydrolysis. The resulting dicar- 'boxylic terminated polymer can be copolymerized with glycols'to form polyesters or with diamines to form polyamides having a graft copolymer structure. Alternatively,

the maleic anhydride or ester terminal group or the polymer can be used in the condensation polymerization with 40 the glycols or diamines. The vicinal hydroxy or carboxyl terminated polymers of the invention can also be copolymerized with epoxy compounds, and the imine compounds, such as ethyleneimine.

The placement of the sidechain in the polymer backbone is dependent on the terminal group of the macromolecular monomer and the reactivity of the comonomer.

The macromolecular monomers of the invention are stable in storage and do not significantly homopolymerize.

Furthermore, the macromolecular monomer copolymerizes through the terminal double bond or reactive end group and is not incorporated into the polymeric backbone by grafting reactions to the polymer of the macromolecular monomer segment.

As indicated hereinabove, the macromolecular mono-v monomers in a predictable manner as determined by relative reactivity ratios. It can be shown that the instantaneous copolymer equation:

simply reduces to the approximation: r M1 when M is in very low molar concentrations.

Thus, the macromolecular monomer (M copolymerby r values and monomer feed compositions. Rearrangement of equation (2) gives:

dM /M Percent conversion M The reactivity ratio, r can be estimated from a relatively low conversion sample of a single copolymerization experiment. The validity of this concept of a predictable and controllable reactivity of the macromolecular monomer can thereby be established. It has been shown that the reactivity of commercial monomers with the macromolecular monomers of the present invention with various end groups correlate with available literature values for reactivity ratios of r The method of the present invention permits the utilization of all types of polymerizable monomers for incorporation into backbone polymers, and makes it possible for the first time to design and build graft copolymers of controlled molecular structure, and of backbone and graft segments with different properties, such as hydrophobic and hydrophilic segments, crystalline and amorphous segments, polar and non-polar segments, segments with widely different glass transition temperatures, whereas prior work on SDS terblock copolymers had been limited to the incompatibility of glassy polystyrene blocks with rubbery polydiene blocks.

The copolymerization of the polymerizable macromolecular monomers With the comonomers may be conducted in a wide range of proportions. Generally speaking, a sufiicient amount of the macromolecular monomer should be present to provide the chemically joining of at least one of the uniform molecular weight sidechain polymers to each backbone polymer, so that a noticeable effect on the properties of the graft copolymeric properties can be obtained. Since the molecular weight of the polymerizable macromolecular monomer generally exceeds that of the polymerizable comonomers, a relatively small amount of the polymerizable macromolecular monomer can be employed. However, the chemically joined, phase separated thermoplastic graft copolymers may be prepared by copolymerizing a mixture containing up to about by weight, or more, of the polymerizable macromolecular monomers of this invention, although mixtures containing up to about 60% by weight of the polymerizable macromolecular monomer are preferred. Stated otherwisejthe resinous thermoplastic chemically joined, phase separated graft copolymer of the invention is comprised of (1) from 1% to about 95% by weight of the polymerizable macromolecular monomer having a narrow molecular weight distribution (i.e., a YEW/Hr: of less than about 1.1), and (2) from 99% to about 5% by Weight of a copolymerizable comonomer defined hereinabove.

The polymerizable macromolecular monomers copolymerize with the hereinabove referred to comonomers in bulk, in solution, in aqueous suspension and in aqueous emulsion systems suitable for the particular polymerizable macromolecular monomer, its end group and the copolymer employed. If a catalyst is employed, the polymerization environment suitable for the catalyst should be employed. For example, oilor solvent-soluble peroxides such as benzoyl peroxides, are generally effective when the polymerizable macromolecular monomer is copolymerized with an ethylenically unsaturated comonomer in bulk, in solution in an organic solvent such as benzene, cyclohexane, hexane, toluene, xylene, etc., or in aqueous suspension. Water-soluble peroxides such as sodium, potassium, lithium and ammonium persulfates, etc. are useful in aqueous suspension and emulsion systems. In the copolymerization of many of thepolymerizable macromolecular monomers, such as those with an ethylenicallyunsaturated end group and a polystyrene, polyisoprene or polybutadiene repeating unit, an'emulsifier or dispersing agent may be employed in aqueous suspension systems. In these systems, particular advantage can be'achieved by dissolving the water-insoluble polymerizable macromolecular monomer in a small amount of a suitable solvent, such as a hydrocarbon. By this novel technique, the comonomer copolymerizes with the polymerizable macromolecular monomer in the solvent, in an aqueous system surrounding the solvent-polymer system. Of course, the

polymerization catalyst is chosen such that it Will be soluble in the organic phase of the polymerization system.

As previously stated, various different catalyst systems can be employed in the present invention for the copolymerization process. It will be apparent to those skilled in the art that the particular catalyst system used in the copolymerization will vary, depending on the monomer feed and the particular end group on the macromolecular monomer. -For example, when using a macromolecular monomer having a vinyl acetate end group, best results are generally obtained by employing free-radical catalyst systems. On the other hand, copolymerization utilizing isobutylene monomer feed with either an allyl, methallyl or epoxy terminated macromolecular monomer, best results are accomplished by utilizing the cationic polymerization techniques. Since the particular polymerizable end group on the macromolecular monomer will depend on the comonorner feed employed because of the relative reactivity ratios, the polymerization mechanism commonly employed for the particular comonomer will be used. For example, ethylene polymerizes under free-radical, cationic and coordination polymerization conditions; propyl ene and higher a'lpha-olefins only polymerize under coordination polymerization conditions; isobutylene only polymerizes under cationic polymerization conditions; the dienes polymerizes by free-radical anionic and coordination polymerization conditions; styrene polymerizes under free-radical, cationic, anionic and coordination conditions; vinyl chloride polymerizes under free-radical and coordination polymerization conditions; vinylidene chloride polymerizes under free-radical polymerization conditions; vinyl fluoride polymerizes under free-radical conditions; tetrafluoroethylene polymerizes under free-radical and coordination polymerization conditions; vinyl ethers polymerize under cationic and coordination polymerization conditions; vinyl esters polymerize under free-radical polymerization conditions; acrylic and methacrylic esters polymerize under free-radical anionic and coordination polymerization conditions; and acrylonitrile polymerizes under free-radical, anionic and coordination polymerization conditions.

It will be understood by those skilled in the art that the solvent, reaction conditions and feed rate will be partially dependent upon the type of catalyst system utilized in the copolymerization process. One of the considerations, of course, will be that the macromolecular monomer be dissolved in the solvent system utilized. It is not necessary, however, for the monomer feed to be soluble in the solvent system. Generally, under these conditions during the formation of the copolymer, the graft copolymer will precipitate out of the solvent wherein it can be recovered by techniques known in the polymer art.

The temperature and pressure conditions during the copolymerization process will vary according to the type of catalyst system utilized. Thus, in the production of low density polyolefin backbones under free-radical conditions, extremely high pressures will be employed. On the other hand, the high density substantially linear polyolefin backbone polymers produced by the coordination type catalyst generally will be prepared under moderately low pressures.

When preparing graft copolymers having a polyolefin backbone of ethylene or propylene or copolymers of ethylene and propylene together with a macromolecular monomer, it is preferred to employ a coordination catalyst known in the art as the Ziegler catalyst and Natta catalysts (the latter being commonly used for polypropylene). That is, materials advanced by Professor Dr. Karl Ziegler of the Max Planck Institute of Mulheim, Ruhr, Germany, and Dr. Giulio Natta of Milan, Italy. Some of these catalysts are disclosed in Belgian Pat. No. 533,362, issued May 16, 1955, and U.S. Pat. Nos. 3,113,115 and 3,257,-

332 to Ziegler et al. These catalysts are prepared by the interaction of a compound of transition metals of group IV-VIII in the periodic table, the catalyst, and an organometallic compound derived from group I-III metals, as eo-catalyst. The latter are compounds such as metal hydrides and alkyls capable of giving rise to hydride ions or carbanions, such as trialkyl aluminum. Compounds of the transition elements have a structure with incomplete d-shells and in the lower valence states, can associate with the metal alkyls to form complexes with highly polarized bonds. Those elements hereinabove referred to as the catalysts are preferably titanium, chromium, vanadium, and zirconium. They yield the best Ziegler catalysts by reaction of their compounds with metal alkyls.

Compounds of these transition metals in the higher valence stage, e.g., titanium tetrachloride, are reduced by the metal alkyls to a lower valence state. The resultant products containing the transition metal in the lower valence state, e.g., titanium dichloride, react directly with the metal alkyl to yield active catalysts possessing hydride ions or carbanions. If the reduction of the transition metal compound proceeds to the free metal, the resultant products are either suitable for catalysis of the displacement reaction, e.g., nickel, cobalt, platinum, or an inactive polymerization catalyst.

Also included among the coordination catalysts contemplated for the copolymerization process of the present invention are those catalyst systems disclosed in the patents assigned to E. I. DuPont de Nemours and Company, i.e., British Pat. No. 778,639, issued July 10, 1957, French Pat. No. 1,134,740, issued Apr. 17, 1957. Belgian Pat. No. 554,475, issued Jan. 24, 1957, British Pat. No. 777,538, issued June 26, 1957, and French Pat. No. 1,135,808, issued May 3, 1957. These patents describe the appropriate catalyst as comprising a compound of one or more of the elements of titanium, zirconium, cerium, vanadium, niobium, tantalum, chromium, molybdenum or tungsten, wherein at least a part of the metal is present in a valence state of three or below and preferably two, or is associated with a sufficient quantity of a reducing agent capable of reducing the valence state of the polyvalent metal to such a lower state. Suitable reducing agents include Grignard reagents, metal alkyls or aryls, zinc metal and metals above zinc in the electromotive series, and the metal hydrides.

As is well-known, the Ziegler catalysts which are effective for the polymerization of ethylene to linear, high density, high molecular weight polyethylene, and the stereospecifie polymerization of other alpha-olefins to crystalline, stereoisomeric polymers are generally heterogeneous.

The various Ziegler catalysts referred to above are approximately equally capable of polymerizing either ethylene, higher alpha-olefins, such as propylene, l-butene, isobutylene, l-pentene, l-hexene, styrene, 3-methyl-1-butene and 4-methyl-l-hexene and conjugated diolefins such as butadiene and isoprene. They can also be used in the copolymerization of any of these monomers with ethylene and other alpha-olefins in conjunction with the macromolecular monomers of the present invention. The difference between the polymerization of ethylene and that of alpha-olefins lies in the possibility of attaining structural regularity in higher polyolefins.

Generally speaking, the production of the high density graft copolymers having olefin backbones will be conducted at pressures of from about 1 to about 1,000 p.s.i., preferably from about 1 to 200 psi. The pressure may be increased by the use of nitrogen gas, if desired.

As previously stated, the solvent system utilized will most conveniently be the solvent employed in the preparation of the macromolecular monomer. Solvents useful for the polystyrene macromolecular monomers are those which dissolve polystyrene. Typical solvents for polystyr ene include cyclohexane, benzene, toluene, xylene, decalin, tetralin, etc.

I The copolymerization reaction may be conducted at any suitable temperature, depending on the particular catalyst, macromolecular monomer, monomer feed, resulting 21 graft copolymer and solvent used. Generally, the graft copolymerization will be conducted at a temperature of from about 10 C. to about 500 C., preferably from about 20 C. to about 100 C.

The graft copolymerization reaction is preferably conducted by placing a predetermined amount of the macromolecular monomer dissolved in the appropriate solvent in the reactor. The polymerization catalyst and monomer are thereafter fed into the solvent system to produce the graft copolymer.

It is generally desirable to provide a graft copolymer having at least about 2% macromolecular monomer incorporated in the backbone polymeric material, however, satisfactory results can be obtained with up to about 40% by weight macromolecular monomer incorporation. Preferably, the graft copolymers of the present invention will have about 5% to about 20% by weight incorporation of the macromolecular monomer into the backbone polymeric material to obtain the optimum physical properties of both the sidechain polymer and the backbone polymer. A

However, graft copolymers having up to about 95% by weight of the macromolecular monomers incorporated therein may be prepared and are contemplated within the scope of the invention.

The means for providing the proper amount of incorporation of the macromolecular monomer can be determined simply by adding the appropriate weighed macro molecular monomer used in the copolymerization process. For example, if a graft copolymer having by weight incorporation of the macromolecular monomer into the backbone polymer is desired, one simply employs 10 parts by weight of the macromolecular monomer for each 90 parts by weight of the monomer feed.

Following the procedures outlined above, graft copolymers having unique combinations of properties are produced. These unique combinations of properties are made possible by the novel process herein which forces the compatibility of otherwise incompatible polymeric segments. These incompatible segments segregate into phases of their own kind.

The chemically joined, phase separated graft copolymers of the invention microscopically possess a controlled dispersion of the macromolecular sidechain in one phase (domain) within the backbone polymer phase (matrix). Because all of the macromolecular monomer sidechain domains are an integral part or interposed 'between large segments of the backbone polymer, the resulting graft copolymer will have the properties of a cross-linked polymer, if there is a large difference in the Tg or Tm of the backbone and side chain segments. This is true only up to the temperature required to break the thermodynamic crosslink of the dispersed phase. In essence, a physically crosslinked (as opposed to chemical cross-linked) type polymer can be made that is reprocessable and whose properties are established by simple cooling, rather than vulcanization or chemical cross-linking.

The graft copolymers of the present invention are dif ferentiated from the macroscopic opaque and weak blends of incompatible polymers of the prior art. The graft copolymers of this invention contain separate phases which are chemically joined and the dispersion of one segment into the matrix polymer is on a microscopic level and below the wavelength of light of the matrix polymer. The graft copolymers herein are, therefore, transparent, tough, and truly thermoplastic.

An illustrative example of the present invention includes combining the advantageous properties of polystyrene with the advantageous properties of polyethylene, although these two polymers normally are incompatible with one another and a mere physical mixture of these polymers has very little strength and is not useful. To combine these advantageous properties in one product, it is necessary that the different polymeric segments be present as relatively large segments. The properties of polystyrene do not become apparent until the polymer consists essentially of at least about 20 recurring monomeric units. This same relationship applies to the polymeric segments present in the graft copolymers herein, i.e., if a graft copolymer comprising polystyrene segments is to be characterized by the advantageous properties of polystyrene, then those polystyrene segments must, individually, consist essentially of at least about 20 recurring monomeric units. This relationship 'between the physical properties of a polymeric segment in its minimum size is applicable to the polymeric segment of all graft copolymers herein. In general, the minimum size of a polymeric segment which is associated with the appearance of the physical properties of that polymer in the graft copolymers herein is that which consists of about 20 recurring monomeric units. Preferably, as noted earlier herein, the polymeric segments both of the copolymeric backbone and the sidechains, will consist essentially of more than about 30 recurring monomeric units. However, as it is well-known, the highly beneficial properties of polymers such as polystyrene are generally apparent when the polymer has a molecular weight of from about 5,000 to about 50,000, preferably from about 10,000 to about 35,000, more preferably 12,000 to about 25,000.

The polymeric segments of the graft copolymers of the invention may themselves be homopolymeric or they may be copolymeric. Thus, a graft copolymer of this invention may be prepared by the copolymerization of ethylene, propylene, and a terminated polystyrene containing a polymerizable alpha-olefin end group. The uninterrupted polymeric segments of the backbone of such a graft copolymer will be copolymeric segments of ethylene and propylene.

The graft copolymers comprising polymeric segments having fewer than about 20 recurring monomeric units are, nevertheless, useful for many applications, but the pre ferred graft copolymers are those in which the various polymeric segments have at least about 20 recurring monomeric units.

Although, as indicated, the graft copolymers herein are characterized by a wide variety of physical properties, depending on the particular monomers used in their preparation, and also on the molecular weights of the various polymer segments within a particular graft copolymer, all of these graft copolymers are useful, as tough, flexible, self-supporting films. These films may be used as foodwrapping material, painters dropcloths, protective wrapping for merchandise displayed for sale, and the like.

Graft copolymers of the macromolecular, monomer, polystyrene, with ethylene-propylene, isobutylene, or propylene oxide monomers have been found to be stable materials that behave like vulcanized rubbers, but are thermoplastic and reprocessable. Thus, an extremely tough, rubbery plastic is obtained without the inherent disadvantages of a vulcanized rubber. These copolymerized rubber-forming monomers with the macromolecular monomers of the present invention have the additional use as an alloying agent for dispersing additional rubber for impact plastics.

Just as metal properties are improved by alloying, so are polymer properties. By adding the appropriate amount of an incompatible material to a plastic in a microdispersed 1 phase, over-all polymer properties are improved. A small amount of incompatible polybutadiene rubber correctly dispersed in polystyrene gives high impact polystyrene. The key to this microdispersion is a small amount of chemical graft copolymer that acts as a flux for incorporating the incompatible rubber.

In a similar manner, a copolymer of the macromolecular monomer of the present invention can be the flux for incorporating or dispersing incompatible polymers into new matrices making possible a whole new line of alloys, impact plastics, malleable plastics, and easy-to-process plastics.

The use of the graft copolymers as alloying agents is particularly exemplified in the case of polyethylene-polystyrene blends. As it is well-known, polyethylene and polystyrene are incompatible when blended together. However, when using the graft copolymers of the present invention as an alloying agent, the polyethylene and polystyrene phases can be conveniently joined.

For example, a blend prepared by mixing 90 to 51 parts. by weight of commercial polyethylene (either low or high density), 10 to 49 parts by weight of commercial polystyrene and to 30 parts by weight of a graft copolymer of the present invention comprising polystyrene sidechains and a polyethylene backbone are useful in making automobile parts, such as inner door panels, kick panels, and bucket seat backs, or appliance parts such as television components. Such blends are also useful as structural foams, sheets and films, containers and lids in packaging, beverage cases, pails, in the manufacture of toys, molded sheets in furniture, hot mold adhesives and computer and magnetic tapes.

The use of the graft copolymers of the present invention as an alloying agent offers a distinct advantage over the prior art blends, inasmuch as the plastic blend can be processed with minimized phase separation of the polystyrene and polyethylene polymers in the blend. The strength of the novel blends of the present invention is also improved over the blends of the prior art.

It polystyrene in the macromolecular monomer is replaced by a poly(alpha-methylstyrene) and is copolym erized with ethylene, a similar polyblend can be prepared as described above. However, these blends will have heat stability which will allow the resulting plastics to be useful in making hot water pipes, sheets in warm areas, and automobile parts, having oxidative stability over rubbercontaining materials. These plastics also have utility in preparing reinforced fiberglass and fillers due to their good adhesion to fiberglass. Polyblends of poly(alphamethylstyrene) graft copolymer with large amounts, i.e., 51-90% by weight of poly(alpha-methylstyrene) and 49% polyethylene, exhibit a higher heat distortion, together with high impact strength and high modulus. These plastics are useful in various engineering applications and in the manufacture of parts for aircraft, auto bodies, recreational vehicles, appliances, gears, bearings, etc.

Another useful blend utilizing the graft copolymers of the present invention comprises mixing 10 to 49 parts of low density polyethylene, 51 to 91 parts by weight of poly(alpha-methylstyrene) and zero to 30 parts by weight of polystyrene and 5 to 30 parts by weight of the graft copolymer of the present invention comprising polyethylene backbone with poly(alpha-methylstyrene) or polystyrene sidechains. The blend is extruded in a mill and the resultant plastic is found useful in making appliances such as colfee makers, humidifiers, high intensity lamps, color television sets, kitchen-range hardware, blenders, mixers, and electric toothbrushes. These plastics are also useful in preparing recreational vehicles such as snowmobile parts and helmets; machine parts such as gears, bearings; plumbing parts such as shower heads, valves, fittings and ballcocks; and motor housing, stamping, lawn sprinklers, stereo tape or cartridges, etc.

The reinforcement of plastics by adding glass fibers or other materials is difficult to achieve because of poor wetting character of many basic polymers. The macromolecular monomers of the present invention, particularly those containing reactive polystyrene, have a tendency to wet and bond to glass With facility. By proper dispersion of glass in a macromolecular copolymer, it is possible to upgrade the bond between the dispersed phase and glass. Thus, the macromolecular graft copolymers of the present invention can also be used as reinforcing adhesion aids to glass fibers.

The invention is illustrated further by the, following examples which, however, are not to be taken as limiting in any respect. In each case, all materials should be pure and care should be taken to keep the reacted mixtures dry and free of contaminants. All parts and percentages, unless expressly stated to be otherwise, are by weight.

PREPARATION OF MACROMOLECULAR MONO- MER SIDECHAINS HAVING UNIFORM MOLEC- ULAR WEIGHT EXAMPLE 1 1 (a) Preparation Of Polystyrene Terminated With Allyl Chloride. A stainless steel reactor is charged with 76.56 parts of A.C.S. grade benzene (thiophene-free), which had been pre-dried by Linde molecular sieves and calcium hydride. The reactor is heated to 40 C. and 0.015 parts of diphenylethylene is added to the reactor by means of a hypodermic syringe. A 12.1% solution of sec-butyl lithium in hexane is added to the reactor portionwise until the retention of a permanent orange-yellow color, at which point an additional 0.885 parts (1.67 moles) of sec-butyl lithium solution is added, followed by the addition of 22.7 parts (218 moles) of styrene over a period of 44 minutes. The reactor temperature is maintained at 36-42" C. The living polystyrene is terminated by the addition of 0.127 parts of allyl chloride to the reaction mixture. The resulting polymer is precipitated by the addition of the alpha-olefin terminated polystyrenebenzene solution into methanol, whereupon the polymer precipitates out of solution. The alpha-olefin terminated polystyrene is dried in an air circulating atmosphere drier at 4045 C. and then in a fluidized bed to remove the trace amounts of methanol. The methanol content after purification is 10 parts per million. The molecular weight of the polymer, as determined by membrane phase osmometry, is 15,400 (theory: 13,400) and the molecular weight distribution is very narrow, i.e., the Hw/Hn is less than 1.05. The macromolecular monomer has the following structural formula:

formula:

'1 cm@ou=om EXAMPLE 2 (a) Preparation Of Poly(alpha-methylstyrene) Terminated With Allyl Chloride.A solution of 472 grams (4.0 moles) of alpha-methylstyrene in 2500 ml. of tetrahydrofuran is treated dropwise with a 12% solution of n-butyl lithium in hexane until the persistence of a light red color. An additional 30 ml. (0.0383 mole) of this nbutyl lithium solution is added, resulting in the development of a bright red color. The temperature of the mixture is then lowered to C., and after 30 minutes at this temperature, 4.5 grams (0.06 mole) of allyl chloride is added. The red color disappears almost immediately, indicating termination of the living polymer. The resulting colorless solution is poured into methanol to precipitate the alpha-olefin terminated poly(alpha-methylstyrene) which is shown by vapor phase osmometry to have a number average molecular weight of 11,000 (theory: 12,300) and the molecular weight distribution is very narrow, i.e., the BTW/71in is less than 1.05. The macromolecular monomer produced has the following structural formula:

wherein n has a value such that the molecular weight of the polymer is 11,000.

The procedure of paragraph (a) is repeated using, in place of n-butyl lithium, a solution of an equivalent amount of potassium t-butyl alkoxylate and in place of alpha-methylstyrene, an equivalent amount respectively of:

(b) 4-vinyl pyridine, terminating with a molar equivalent of allyl chloride to produce a polymer having the following structural formula:

((1) methyl methacrylatc, terminating with vinylbenzyl chloride to produce a polymer having the following struc- (e) N,N-dimethylacrylamide, terminating with p-vinylbenzyl chlorideto produce a polymer having the following structural formula:

. tural formula:

Preparation Of Polystyrene Terminated With Vinyl Chloroacetate A solution of one drop of diphenyl ethylene in 2500 ml. of cyclohexane at 40 C. is treated portionwise with a 12% solution of sec-butyl lithium in cyclohexane until the persistence of a light red color, at which point an additional 18 ml. (0.024 mole) of the sec-butyl lithium is added, followed by 312 grams (3.0 moles) of styrene The temperature of the polymerization mixture is maintained at 40 C. for 30 minutes, whereupon the living polystyrene is capped by treatment with 8 ml. (0.040 mole) of diphenyl ethylene, then terminated by treatment with 6 ml. (0.05 mole) of vinyl chloroacetate. The resulting polymer is precipitated by addition of the cyclo hexane solution to methanol and the polymer is separated by filtration. Its number average molecular weight, as determined by vapor phase osmometry, is 12,000 (theoryz 13,265), and the molecular weight dis- 26 tribution is very narrow, i.e., the JTW/llfn is less than 1.06. The macromolecular monomer produced has the following structural formula:

r '1 10 onaomcna oHoH,-( H- cH, -omo oorr=cm wherein n has a value such that the molecular weight of the polymer is 12,000.

EXAMPLE 4 Preparation Of Poly(alpha-methylstyrene) Terminated With Vinyl Chloroacetate A solution of 357 grams (3.0 moles) of alpha-methylstyrene in 2500 ml. of tetrahydrofuran is treated dropwise with a 12% solution of t-butyl lithium in pentane until the persistence of a light red color. Thereupon, an additional 15.0 ml. (0.03 mole) of the t-butyl solution is added, resulting in the development of a bright red color. The temperature of the mixture is then lowered to 80 C., and after 30 minutes at that temperature, 5.6 ml. of diphenyl ethylene is added. The resulting mixture is poured into 5.0 ml. (0.04 mole) of vinyl chloroacetate and the thus-terminated poly(alpha- 0 methylstyrene) is precipitated with methanol and separated by filtration. Its number average molecular weight, as determined by vapor phase osmometry, is 14,280 (theory: 12,065) and the molecular weight distribution is very narrow. The macromolecular monomer produced has the following structural formula:

I- on? 2 onion, (CH3) CHCH e-cm CH; 0 o CH=CH1 wherein n has a value such that the molecular weight of the polymer is 14,280.

EXAMPLE 5 Preparation Of Polystyrene Terminated With Vinyl-2-Chloroethyl Ether A solution of one drop of diphenyl ethylene at 40 C. is treated portionwise with a 12% solution of t-butyl lithium in pentane until the persistence of a light red color, at which point an additional 30 ml. (0.04 mole) of the t-butyl lithium solution is added, followed by 312 grams (3.0 moles) of styrene. The temperature of the polymerization mixture is maintained at 40' C. for

30 minutes, whereupon the living polystyrene is terminated by treatment with 8 ml. (0.08 mole) of vim chloroethyl ether. The resulting polymer is precipitated by addition of the benzene solution to methanol and the polymer is separated by filtration. Its number aver- 'age molecular weight, as determined by vapor phase osmometry, is 7,200 (theory: 7,870) and the molecular 27 weight distribution is very narrow, i.e., the 'JlTw/lTn is less than 1.06. The macromolecular monomer produced has the following structural formula:

(CH3); C CHz C H CHz CH: O CH=CH1 wherein n has a value such that the molecular weight of the polymer is 7,200.

EXAMPLE 6 Preparation Of Polystyrene Terminated With Epichlorohydrin A benzene solution of living polystyrene is prepared in Example and terminated by treatment with 10 grams (0.10 mole) of epichlorohydrin. The resulting terminated polystyrene is precipitated with methanol and separated by filtration. Its molecular weight, as shown by vapor phase osmometry, is 8,660 (theory: 7,757) and its number average molecular weight distribution is very narrow. The macromolecular monomer produced has the following structural formula:

wherein n has a value such that the molecular weight of the polymer is 8,660.

EXAMPLE 7 (a) Preparation Of Polystyrene Terminated With Methacrylyl Chloride:

To a solution of 0.2 ml. of diphenyl ethylene in 2500 ml. of benzene there is added dropwise a 12% solution of n-butyl lithium in hexane until the persistence of a light reddish-brown color. An additional 24 ml. (0.031 mole) of this n-butyl lithium solution is added, and then, 416 grams (4.0 moles) of styrene, resulting in the development of an orange color. A temperature of 40 C. is maintained throughout by external cooling and by controlling the rate at which the styrene is added. This temperature is maintained for an additional 30 minutes after all of the styrene has been added, and then is lowered to C., whereupon 4.4 grams (0.1 mole) of ethylene oxide is added, causing the solution to become colorless The living polymer is terminated by reaction with 10 ml. (0.1 mole) of methacrylyl chloride. The resulting polymer has a number average molecular weight as shown by vapor phase osmometry of 10,000. The macromolecular monomer has the following structural formula:

wherein n has a value such that the molecular weight of the polymer is 10,000.

(b) Acrylyl chloride is substituted for methacrylyl chloride in the above procedure to give an acrylic acid ester end group on the polystyrene chain.

(c) Allyl chloride is substituted for methacrylyl chloride in procedure (a) to produce an allyl ether terminated polystyrene.

(d) Methallyl chloride is substituted for methacrylyl chloride in procedure (a) to produce methallyl ether terminated polystyrene.

(e) Maleic anhydride is substituted for methacrylyl chloride in procedure (a), followed by protonation with water to produce polystyrene terminated with the half ester of maleic acid.

(f) Epichlorohydrin is substituted for methacrylyl chloride to produce an epoxy ether terminated polystyrene.

(g) The procedure of (a) is repeated using in place of styrene, an equivalent amount of isoprene and in place of n-butyl lithium an equivalent amount of sec-butyl lithium to produce primarily a rubbery cis-l,4-polyisoprene. The low Tg living polymer is terminated by the addition of a molar equivalent, based on sec-butyl lithium, ethylene oxide as a capping agent, followed by a molar equivalent amount of allyl chloride to produce a polymer predominantly having the following structural formula:

EXAMPLE 8 Preparation Of Polystyrene Terminated With Methacrylyl Chloride A stainless steel reactor is charged with 32 gallons of A.C.S. grade benzene (thiophene-free), which had been predried by Linde molecular sieves and calcium hydride. The reactor is heated to a temperature of between 38-40 C. and 10 ml. of diphenyl ethlyene is added to the reactor by means of a hypodermic syringe. An 11.4% solution of secondary butyl lithium in hexane is added to the reactor portionwise until the retention of a permanent orangeyellow color is obtained (60 ml.), at which point an additional 3.44 pounds of the secondary butyl lithium in hexane is added to the reactor, followed by the addition of 82.5 pounds of purified styrene over a period of 1 hour and 40 minutes. The reactor temperature is maintained at 3840 C. The living polystyrene is capped by the addition of 0.28 pounds of ethylene oxide and the reaction solution changes from a red-orange color to yellow. The resulting capped living polystyrene is thereafter reacted with 260 ml. of methacrylyl chloride and the solution changes to a very pale yellow color. The methacrylate terminated polystyrene is precipitated by the addition of the polymer benzene solution into methanol, whereupon the polymer precipitates out of solution. The polymer is dried in an air circulating atmosphere drier at 40-45 C. and then in a fluidized bed to remove the trace amounts of methanol. The molecular weight of the polymer as determined by membrane phase osmometry, is 13,400 and the molecular weight distribution is very narrow, i.e., the Hw/Hn is less than 1.05.

EXAMPLE 9 Preparation Of Polystyrene Terminated With Maleic Anhyride A stainless steel reactor is charged with 2.5 liters of A.C.S. grade benzene (thiophene-free), which had been predried by Linde molecular sieves and calcium hydride. The reactor is heated to 40 C. and 0.2 ml. of diphenyl ethylene is added to the reactor by means of a hypodermic syringe. A 12.1% solution of sec-butyl lithium in hexane is added to the reactor portionwise until the retention of a permanent orange-yellow color is obtained (0.7 ml.), at which point an additional 22.3 ml. of sec-butyl lithium solution is added, followed by the addition of 421.7 grams of styrene over a period of 16 minutes. The reactor temperature is maintained at 40-45 C. Five minutes after styrene addition is completed, ethylene oxide is added from a lecture bottle sub-surface intermittently until the solution is water white. One hour after ethylene oxide addition is complete, 20.55 ml. of maleic anhydride-benzene solution (the maleic anhydride solution was prepared Sec-Buty1 CH (llH cH cHg 0 a CH a. HO C/ a ll EXAMPLE Preparation Of Polybutadiene Terminated With Allyl Chloride C.P. grade 1,3-butadiene (99.0% purity) is condensed and collected in l-pint soda bottles. These bottles had been oven baked for four hours at 150 C., nitrogen purged during cooling, and capped with a perforated metal crown cap using butyl rubber and polyethylene film liners. These bottles containing the butadiene are stored at 10 C. with a nitrogen pressure head (10 p.s.i.) in a laboratory freezer before use. Hexane solvent is charged to the reactors and heated to 50 C., followed by the addition of 0.2 ml. of diphenyl ethylene by way of a syringe. Secondary butyl lithium is added dropwi'se via syringe to the reactor until the red diphenyl ethylene anion color persists for at least about 10-l5 minutes. The reactor temperature is lowered to 0 C., and 328.0 grams of butadiene is charged into the polymerization reactor, followed by the addition of 17.4 ml. (0.02187 mole) of a 12% secondary butyl lithium solution in hexane, when half of the butadiene charge has been added to the reactor. The butadiene is polymerized for 18 hours in hexane at 50 C. Following the polymerization, 400 ml. portions of the anionic polybutadiene solution in the reactor is transferred under nitrogen pressure into capped bottles. Allyl chloride (0.48

ml., 0.00588 mole) is injected into each of the bottles. The bottles are clamped in water baths at temperatures of 50 C. and 70 C. for periods of time ranging up to 24 hours. The samples in each of the bottles are short stopped with methanol and Ionol solution and analyzed by Gel Permeation Chromatography. Each of the samples is water white and the analysis of the Gel Permeation Chromatography scans reveals that each of the samples had a narrow molecular weight distribution.

Several comparison samples were conducted in bottles coming from the same lot of living polybutadiene, which were capped with 2-chlorobutane (0.4 ml., 0.00376 mole) as the terminating agent. The resulting polymers terminated with 2-chlorobutane were yellow in color and after standing for a period of 24 hours at 70 C., appeared to have a broad molecular weight distribution as revealed by the Gel Permeation Chromatography scan. It is clear that the reaction and reaction product of 2-chlorobutane with anionic polybutadiene are different than the reaction and reaction product of allyl chloride and anionic polybutadiene.

EXAMPLE 11 Preparation Of Methacrylate Terminated Polyisoprene A one-gallon Chemco glass-bowl reactor is charged with 2.5 liters of purified heptane which had been predried by a Linde molecular sieve and calcium hydride, followed by the addition of 0.2 ml. of diphenyl ethylene as an indicator and the reactor is sterilized with the dropwise addition of tertiary butyl lithium solution (12% in hexane) until the retention of the characteristic light yellow color is obtained. The reactor is heated to 40 C. and 19.9

ml. (0.025 mole) of a 12% solution of tertiary butyl lithium in hexane is injected into the reactor via hypodermic syringe, followed by the addition of 331.4 grams (4.86 moles) of isoprene. The mixture is allowed to stand for one hour at 40 C. and 0.13 mole of ethylene oxide is charged into the reactor to cap the living polyisoprene. The capped living polyisoprene is held at 40 C. for 40 minutes, whereupon 0.041 mole of methacrylyl chloride is charged into the reactor to terminate the capped living polymer. The mixture is held for 13 minutes at 40 0., followed by removal of the heptane solvent by vacuum stripping. Based upon the Gel Permeation Chroma tography scans for polystyrene, the molecular weight of the methacrylate terminated polyisoprene by Gel Permeation Chromatography was about 10,000 (theory: 13,000). The methacrylate terminated polyisoprene macromolecular monomer had a structural formula represented as follows:

EXAMPLE 12 Preparation Of Alpha-Olefin Terminated Polyisoprene A one-gallon Chemco glass-bowl reactor is charged with 2.5 liters of purified heptane which had been predried by a Linde molecular' sieve and calcium hydride, followed by the addition of 0.2 ml. of diphenyl ethylene as an indicator. The reactor and solvent are sterilized by the dropwise addition of tertiary butyl lithium solution (12% in hexane) until the retention of the characteristic light yellow color is obtained. The reactor is heated to 40 C. and 19.03 ml. (0.02426 mole) of tertiary butyl lithium solution is injected into the reactor via hypodermic syringe, followed by the addition of 315.5 grams (4.63 moles) of isoprene. The polymerization is permitted to proceed at 50 C. for 66 minutes and at this time 2.0 ml (0.02451 mole) of allyl chloride is added to the hvmg polyisoprene. The terminated polyisoprene is held at 50 C. for 38 minutes, whereupon the polymer is removed from the reactor to be used in copolymerization reactions. The polymer was analyzed by Gel Permeation Chromatography and had a very narrow molecular weight distribution, i.e., an iTw/Hn of less than about 1.06. The theoretical molecular weight of the polymer is 13,000. The polymerizable macromolecular monomer had a structural formula represented as follows:

CH: H n

EXAMPLE 13 Polymerization 0f Styrene With Vinyl Lithium To a one gallon Chemco reactor, there is added 2500 ml. of tetrahydrofuran and cooled to 15 C., at which time 6.5 ml. of a 11.2% solution of vinyl lithium in tetrahydrofuran (0.2 mole lithium) is added to the reactor, imparting a light tan color to the solution. The vinyl lithium was purchased from Alpha Inorganics Ventron of Beverly, Massachusetts, as a two molar solution in tetrahydrofuran. Analysis of the solution by several methods showed that the solution contained 11.2% active lithium. After the vinyl lithium solution is added, a 0.25 mole styrene charge is added to the reactor via syringe with the observation of a small exotherm of about 1 C. (the reactor temperature is controlled by liquid nitrogen cooling coils inside the reactor at a temperature of 15 0.). Ten minutes after the styreneis added, 3.6 ml. of water is added to the reactor, resulting in an almost immediate change in color from deep orange-brown to water white and a considerable gas evolution is observed (the internal pressure in the reactor increased from 8 p.s.i.g.). A sample is taken from the head space (about 2.5 liters in volume) and from the liquid phase at the same time (the two samples are analyzed and identified as containing large amounts of ethylene). The styrene polymer is Withdrawn from the reactor and analyzed. The GPC molecular weight of the polystyrene is 108,000, as measured against the Pressure Chemical Company sample 2(b) standard certified as Hw/Hn=l.06,

and Hn=20,200:600. Measured against the same standard, the weight average molecular weight of the polymer is 99,000 and the number average molecular weight is 66,000. The polydispersity of the polymer is 1.49. Based upon the limiting polydispersity of about 1.33 for living polymers, as indicated in Henderson et al., Macromolecular Reviews, Vol. 3, Interscience Publishers, page 347 (1968), several side reactions obviously occur when using vinyl lithium as a polymerization initiator. In addition, the broad molecular weight distribution and the inability to control the molecular Weight of the polymer is indicative that the initiation rate of vinyl lithium is extremely slow. Accordingly, the vinyl lithium initiated polystyrene is not suitable in the preparation of the graft copolymers of the present invention in preparing chemically joined, phase separated graft copolymers, which have sidechains of controlled and uniform molecular weights.

Attempted copolymerization of the vinyl lithium initiated polystyrene with methyl methacrylate and 'acrylonitrile under free-radical conditions only results in a mixture of polystyrene and the respective poly(methyl methacrylate) or polyacrylonitrile. Also, attempted copolym rization of the alpha-olefin terminated polystyrene of Example 1(a) with methyl methacrylate and acrylonitrile under free-radical conditions only resulted in a mixture of homopolymers as determined by IR analysis of the benzene and cyclohexane extracts. This result is expected due to the inability of alpha-olefins to polymerize under free-radical conditions.

PREPARATION OF GRAFT COPOLYMERS HAV- ING MACRO'MOLECULAR MONOMERS INTE- GRALLY POLYMERIZED INTO THE BACKB-ONE EXAMPLE 14 Preparation Of Graft Copolymer From Poly(alphamethylstyrene) Macromolecular Monomer Terminated With Allyl Chloride And Ethylene A solution of grams of poly(alpha-methylstyrene) macromolecular monomer terminated with allyl chloride and having an average molecular weight of 10,000 prepared as in Example 2(a) in 100 ml. of cyclohexane is prepared and treated with 5.5 ml. of 0.645 M (9.1% solution) diethyl aluminum chloride in hexane and 2 ml. of vanadium oxytrichloride, then pressured with ethylene to 30 p.s.i.g. This system is agitated gently for about one hour at 30 C., whereupon a polymeric material precipitates from the solution. It is recovered by filtration and pressed into a thin transparent film which is tough and flexible.

EXAMPLE 15 (a) Preparation Of Graft Copolymer Having A Polyethylene Backbone And Polystyrene Sidechains.-One gram of the alpha-olefin terminated polystyrene of uniform molecular weight prepared in Example 1(a) is dissolved in 1500 ml. of cyclohexane and charged into a 2- liter Chemco reactor. The reactor is purged with prepurified nitrogen for 30 minutes, and 22 ml. of 25% ethylaluminum sesquichloride solution (in heptane) is added. The reaction is pressured to 40 p.s.i. with 20 grams of ethylene into the solution. Thereafter, 0.1 ml. of vanadium oxytrichloride is added and the ethylene pressure drops from 4D p.s.i. to 1 p.s.i. in about 1 minute. The reaction is terminated in 3 minutes by the addition of isopropanol. The polymer is recovered by filtration and slurried with cyclohexane and then with isopropanol. The yield is 18.0 grams of a fluffy, white copolymer having a macromolecular monomer sidechain content of 5.8%, as determined by I.R. Extraction and analysis of the extracts indicate all of the macromolecular monomer and 17.0 grams of the ethylene copolymerized.

(b) The procedure in Example 15 (a) is repeated, except that 2.0 grams of the macromolecular monomer is used instead of 1.0 gram. The yield of the copolymer is 20.5 grams and the macromolecular monomer sidechain content, as determined by I.R., is 10%.

EXAMPLE 16 (a) Preparation Of Graft Copolymer Having A Polyethylene Backbone And Polystyrene Sidechains.-A 2- liter Chemco reactor is charged with 1500 ml. of purified cyclohexane. 20 grams of alpho-olefin terminated polystyrene prepared in Example 1(a) is added and dissolved in the purified cyclohexane. The reactor is thereafter purged with prepurified nitrogen for one hour with concurrent slow agitation. Ethylene is added to the reactor at the rate of 5 liters per minute to a pressure of 5 p.s.i. The contents of the reactor is heated and controlled at 25 C., and high speed stirring is started; ethylaluminum sesquichloride (22.8 ml., 25% in heptane) catalyst is injected into the reactor by a hypodermic syringe, followed by the addition of 0.1 ml. of vanadium oxytrichloride. Polymerization begins immediately and the ethylene pressure in the reactor drops to nearly zero in about a minute. At this point, the ethylene rate is reduced to 0.5 liter per minute, and cooling is used to maintain a temperature of 25 C. At the end of one hour, a total of 43 grams of ethylene has been charged into the reactor, and the reactor is full of a fiuffy polymer slurry. The reaction is stopped by the addition of 50 ml. of isopropanol to inactivate the catalyst.

The polymer is recovered by filtration, slurried and boiled in 1.5 liters of benzene for one hour, then re-filtered to remove all the unreacted alpha-olefin terminated polystyrene from the copolymer. The polymer is then slurried in 1.5 liters of isopropanol and 0.03 gram of Irganox 1010 anti-oxidant is added and then filtered and dried in a vacuum oven at 50 C. The yield is 49 grams of a fluffy, white copolymer having an alpha-olefin terminated polystyrene content of 16%, as determined by IR. of a pressed film.

(b) Preparation of Graft Copolymer Having A Polyethylene Backbone And Poly(alpha-methylstyrene) Sidechains.The macromolecular monomer used to produce the sidechains is first prepared by repeating the procedure described in Example 2(a), except that in place of the n-butyl lithium, 14 ml. (0.0178 mole) of sec-butyl lithium (12% solution in heptane) is used as the initiator. The number average molecular weight, as determined by gel permeation chromatography, is 26,000 (theory: 26,500) and the molecular Weight distribution is very narrow, i.e., the fiTw/Hn is less than 1.05.

Four liters of cyclohexane (Phillips polymerization grade) and 200 grams of the alpha-olefin terminated poly- (alpha-methylstyrene) macromolecular monomer produced as described above are charged into a Chemco reactor. The mixture is heated to 70 C. with concurrent stirring to dissolve the macromolecular monomer. The reactor is purged with high purity nitrogen for one hour with stirring. Ethylene gas is introduced into the reactor to a pressure of 5 p.s.i., followed by 228 ml. of ethyl-aluminum sesquichloride (25% in heptane) and 1.0 ml. vanadium oxytrichloride. Agitation is increased and polymerization begins immediately, as noted by the pressure in the reactor dropping to nearly zero. The ethylene flow rate is adjusted to 5 liters per minute, and the internal temperature is controlled at 70 C. At the end of one hour, the reaction is terminated by the addition of 500 ml. of isopropanol to inactivate the catalyst,

The polymer is isolated by centrifugation, slurried with benzene for one hour, and recentrifuged. The copolymer is then slurried in liters of methanol and 0.3 gram of Irganox 1010 for one hour, centrifuged and dried in an oven at 50 C. The yield is 260 grams having an alphaolefin terminated poly(aIpha-methylstyrene) content of 22%, as determined by LR. analysis of a pressed film.

EXAMPLE 17 Preparation of Graft Copolymer Having An Ethylene- Propylene Copolymeric Backbone And Polystyrene Sidechains A 2-liter Chemco reactor is charged with 1 /2 liters of dry benzene and 50 grams of poly(alpha-methylstyrene) terminated with allyl chloride (as prepared in Example 2). The macromolecular monomer is dissolved by stirring and thereafter purged with nitrogen. The reactor is then charged with ethylene and propylene gases at the rate of 200 m1./minute and 800 ml./minute, respectively, to build-up p.s.i. pressure in the reactor. While maintaining a reaction temperature of 25-35 C., 2 ml. of vanadium oxytrichloride and 4 ml. of ethylaluminum sesqui chloride solution (25% in heptane) are added to the reaction mixture by means of syringe to initiate polymerization. -As the polymerization is started, additional macromolecular monomer (335 ml. of 10% macromolecular solution) is added in solution form, i.e., 70 grams of the macromolecular monomer is dissolved in 630 ml. of dry benzene, and pumped in by Micro-Bellow-pump. During the reaction, the flow rate of the gases are checked constantly to insure that the ethylene and propylene feed rate are at the same initial level. Additional catalyst, Et A1 C1 (27 ml. in 25% heptane) and VOCl (1.8 ml.) is

added by syringe during the reaction, as the rate of polymerization slowed down, which is observed by a build-up of the internal pressure in the reactor. After one hour, the

polymerization is terminated by the addition of 20 ml. of

isopropyl alcohol. The product is precipitated in methanol and 51 grams of a white rubbery polymer is obtained. EXAMPLE 18 Preparation Of Graft Copolymer Having Ethylene-Propylene Copolymeric Backbone And Polystyrene Sidechains A l-gallon Chemco reactor is charged with 3 liters of dried cyclohexane and 10 grams of polystyrene terminated with allyl chloride (as prepared in Example 1). The solution is purged with nitrogen for 30 minutes. 20 ml. of trin-hexylaluminum (25 solution is added, followed by the addition of 139.5 grams of propylene to obtain a pressure of 26 p.s.i. and 20.4 grams of ethylene to obtain a pressure of 48 p.s.i. Finally, there is added 0.2 ml. of vanadium oxytrichloride and a drop in pressure is observed. The polymerization is terminated after 10 minutes by the addition of 10 ml. of isopropanol.

The terpolymer solution is added slowly, with stirring to a 4-liter beaker containing methanol to coagulate the polymer. The polymer which separated is air dried overnight. To remove the trace of catalyst residue, the gray colored polymer is dissolved in 500 ml. of cyclohexane and placed in a 2-liter resin flask, together with 1 liter of distilled water containing 0.1 gram of NaOH, and refluxed at 80 C. for 2 hours. The contents are transferred into a 2-liter separatory funnel, and the bottom water layer is drained. The upper cyclohexane layer is added to methanol slowly, with stirring, to coagulate the polymer. The recovered polymer is dried in a vacuum oven. The unreacted macromolecular monomer is removed from the dried polymer by first dissolving in cyclohexane and adding dropwise to ethyl ethyl ketone, with stirring. The terpolymer which is insoluble in methyl ethyl ketone is filtered and dried in a vacuum oven, and a yield of 52 grams is obtained. The terpolymer has improved tensile strength compared to ethylene-propylene copolymers prepared in the same manner without the macromolecular monomer.

34 (EXAMPLE 19 Preparation Of Graft Copolymer Having Polyisoprene Backbone And Polystyrene Sidechains 500 ml. of dried cyclohexane is charged into a reactor, followed by the addition of 100 l. (68 grams) of freshly distilled isoprene (Phillips polymerization grade), together with 17 grams of polystyrene terminated with allyl chloride (as prepared in Example 1). The reactor is sealed, followed by the addition of 2.5 ml. of tri-n-hexylaluminum solution (25 in heptane) and 0.16 ml. of titanium tetrachloride with hypodermic syringes. The reactor is agitated at 55 C. for 16 hours, whereupon the contents of the reactor are slowly poured, with stirring, into a 4-liter beaker containing 2 liters of a 1% solution of Ionol antioxidant in isopropanol. A tough, rubbery, copolymer is obtained.

EXAMPLE 20 Preparation Of Graft Copolymer Having A Polystyrene Backbone And Polyoxyethylene Sidechains Equal parts of the polyoxyethylene terminated with vinylbenzyl chloride prepared in Example 1(c) and styrene monomer are placed in a reactor containing 1,000 ml. of benzene. The reactor is heated to 60 C. and one part by weight of azobisisobutyronitrile free-radical polymerization catalyst is added. The polymerization is complete in three hours, obtaining a graft copolymer having hydrophilic-hydrophobic properties. The graft copolymer also reduces hydrostatic charges and is an alloying agent for polystyrene and polyoxyethylene.

EXAMPLE 21 Preparation of Graft Copolymer Having A Polypropylene Backbone And Cis-l,4-Polyisoprene Sidechains A l-gallon Chemco reactor is charged with 3 liters of heptane and 10 grams of allyl ether terminated sis-1,4- polyisoprene (as prepared in Example 7(g) The macromolecular monomer is dissolved by stirring and thereafter the solution is purged with nitrogen for 30 minutes. 10 ml. of diethylaluminum chloride (25% solution in heptane) is added, followed by the addition of 0.3 gram of TiCl 139.5 grams of propylene is added to obtain a pressure of 26 p.s.i. The reactor is heated to 60 C., and polymerization is terminated after 18 hours, whereupon the contents of the reactor are slowly poured, with stirring, into a 4-liter beaker containing 2 liters of 1% solution of Ionol antioxidant in isopropanol. The graft copolymer has higher impact properties than polypropylene homopolymer.

EXAMPLE 22 Preparation Of Graft Copolymer Having Polyisobutylene Backbone And Polystyrene Sidechains To a solution of 20 grams of polystyrene macromer terminated with epichlorohydrin and having an average molecular weight of 10,000 in 1,000 ml. of toluene at -70 0., there is added grams of isobutylene. 45 ml. of boron trichloride ethyl ether complex is added slowly, the temperature being maintained at 70 C. throughout. Polymerization occurs as the catalyst is added and is complete almost immediately after all of the catalyst has been added. The resulting graft copolymer is obtained by evaporating away the toluene and washing the residual solid with methanol.

EXAMPLE 23 Preparation Of Graft Copolymer Having Polyisobutylene Backbone And Polystyrene Sidechains To 1,000 ml. of methyl chloride at -70 C. there is added 10 grams of polystyrene macromer terminated with epichlorohydrin, having an average molecular weight of 10,000. To this resulting solution maintained at -70 C., there is added concurrently and dropwise, a solution of 2 grams of aluminum chloride in 400 ml. of methyl chloride and '90 grams of isobutylene. The time required for these '35 additions is one hour and at the end of this time polymerization is substantially complete. The resulting insoluble graft copolymer is isolated by evaporation of the methylene chloride. Similar results are obtainable by employing either a methallyl or methacrylyl end group on the polystyrene such as the product prepared in Examples 1(b), 7(a) and 7(d).

EXAMPLE 24 (a) Preparation Of Polystyrene Macromolecular Monomer, Capped With Butadiene And Terminated With Allyl Chloride. 2.5 liters of benzene (thiophene-free) are charged into the reactor and heated to 40 C. 0.2 ml. of diphenyl ethylene is added as an indicator and the reactor is sterilized with dropwise addition of a 12% solution of sec-butyl lithium until the persistence of an orangered color. At this point, an additional 18 ml. (0.024 mole) of sec-butyl lithium solution (12% in hexane) is added, followed by 416 grams (4.0 moles) of styrene. The temperature of the polymerization mixture is maintained at 40 C. for minutes. Then the living polystyrene is capped with butadiene by bubbling butadiene gas into the reactor until the color of the solution changes from dark red to orange. The living polymer is terminated by treatment with 4.1 ml. (0.05 mole) of allyl chloride. The macromolecular monomer thus prepared is precipitated with methanol and separated by filtration. It number average molecular weight estimated from gel permeation chromotography is 25,000 (theory: 18,000) and molecular weight distribution is very narrow. The macromolecular monomer produced has the following structural formula:

CH CHz- (l3 Il CH; lCET E-CH CH: (DH-CH1} CHz-C H: CH1

on: m

where m equals 1 or 2.

(b) Preparation Of Graft Copolymer Having A Polyethylene Backbone And Polystyrene Sidechains-2 grams of butadiene capped, alpha-olefin terminated polystyrene macromolecular monomer as prepared in Example 24(a) above, is dissolved in 1500 ml. of cyclohexane and charged into a 2-liter Chemco reactor. The reactor is purged with prepurified nitrogen for 30 minutes, and 2 ml. of 25% ethylaluminum sesquichloride solution (in heptane) is added. The reactor is pressurized with 21 grams of ethylene to 40 p.s.i. Thereafter, 0.1 ml. of vanadium oxytrichloride is added and ethylene pressure is dropped from 40 p.s.i. to 1 p.s.i. in about 1 minute. The reactor is terminated in 3 minutes by the addition of isopropanol. The polymer is recovered by filtration.

It is known that the physical properties of linear high density polyethylene are dependent on its extent of crystallinity, molecular weight and molecular weight distribution. It is a balance of these characteristics that generally governs the end use properties of fabricated items. The graft copolymers of the present invention, particularly those having a polyethylene backbone and polystyrene sidechains, modifies the physical properties of polyethylene without affecting the beneficial crystalline properties of polyethylene.

In order to demonstrate these beneficial properties of the graft copolymers, as well as the crystalline nature of the copolymers, several tests were conducted. The following data illustrates the properties of graft copolymers having a polyethylene backbone and polystyrene sidechains prepared by the procedure described in Examples 9 and 10.

Determination Of Macromolecular Monomer Content By LR. Spectroscopy Calibration curve of ethylene/polystyrene macromolecular monomer copolymer.

Commercial high density polyethylene, U.S.I. Microthene ML 708 and Dow polystyrene, Styron 666a are blended in the ratios: /20, 70/30, 60/40, and 50/50, and extruded twice through a Killon extruder. The extruded blends are pressed into thin films (about one mil) and the infrared spectrum run on a Beckman IR. 12 infrared spectrophotometer. The benzene ring absorbance at 710 cmf and the methylene absorbance at 1480 cm? are measured and the ratios calculated. The calibration curve is drawn by plotting absorbance ratio vs. percent styrene.

Determination Of Macromolecular Monomer Content Of Copolymers Ethylene-macromolecular monomer copolymers are pressed into thin films and their IR. spectrum obtained on the Beckman IR. 12 spectrophotometer. The absorbance at 710 cm. for polystyrene-macromolecular monomer is compared to absorbance at 1480 cmr and the macromolecular monomer is determined from the calibration curve. The LR. spectra is evidence that a graft copolymer having a polyethylene backbone and polystyrene sidechains (M.W. 27,000) having 20% by Weight incorporation.

Sample Preparation And Testing The copolymers are compression molded into sheets of about 20 mil thickness for stress-strain testing. The mold is two 7" x 7" x 0.040" steel plates separated by a 7" x 7" x 0.020" steel shim cut out to make a 5" x 5" .x 0.020" center cavity. Surfaces are coated with Dow Corning R-671 Resin as a mold release.

Approximately eight grams of polymer are placed in the mold, and molded at 400 F. for 10 minutes at 30 tons pressure, and cooled down by circulating water.

Three test specimens are cut out of the sheet with a dumbbell C die (ASTM D412-67T) and dimensions are measured by a micrometer.

Tensile properties are obtained on an Instron Tester according to ASTM D638 at a cross head speed of 2 inches/ minute. 1

Flexual modulus of the copolymers is obtained on bars with Instron Tester according to ASTM D790.

DGIieat deflection is obtained on bars acording to ASTM Crystalline Structure Of Graft Copolymer Of Polyethylene Backbone And Macromolecular Monomer Sidechains The crystalline nature of copolymers having polyethylene backbones is studied from:

Crystallinity X-ray diffraction;

Melting behaviorDifferential Scanning Calorimetry; Crystallite orientation-X-ray diffraction; and Spherulite formationLight microscopy.

crystallinity The measurement of crystallinity by X-ray diffraction takes many forms but an effective simple method is to calculate a crystallinity index (CrI) as follows:

CrI I where I is the intensity, above background scattering, of the 110 diffraction peak taken at 2l.6 20. I is the amorphous scattering at 198 20.

For polyethylene, the separation of the X-ray scattering ascribed to the crystalline and amorphous fractions is: simplified, since the amorphous peak is clearly distin-- guished from the crystalline peaks on diflraction patterns. A diifractorner tracing of a polyethylene with 12% integrally copolymerized alpha-olefin terminated polystyrene shows the separation of the two fractions and the measurement of peak heights. When used on published diffraction patterns of polyethylene, the metheil gives, erystal- 3 7 linity values in accord with those in which the authors used integrated intensity measurements for the respective crystalline and amorphous material.

CrI values of several polyethylenes ranged from 7277. The CrI of polyethylene decreases for copolymers in proportion to macromolecular monomer content (6- 30%). It is significant, that within experimental error, CrI values are not lower than those expected by a simple dilution of the polyethylene crystallinity with an amorphous macromolecular monomer.

The diifractometer tracings used for the CrI measurements are also inspected for crystal lattice changes and for diffraction line-broadening with macromolecular monomer addition. Changes in the crystal lattice are not observed, which means that the macromolecular monomer is not incorporated into the polyethylene crystal lattice, but rather in the amorphous regions of the sample. Measured half-width of the 200 diffraction peak shows no decrease in crystallite size with macromolecular monomer addition. Thus, diffractometer tracings, such as the one with 12% macromolecular copolymer, and the graph of CrI versus macromer content demonstrate a significant feature of the invention; namely, that the crystallinity of the polyethylene fraction is maintained in the presence of the macromolecular monomer.

Melting Behavior Of Marcomolecular Monomer-Polyethylene Copolymers A differential scanning calorimeter (DSC) is used to determine the melting behavior of the copolymers and to seek confirmation of the lack of interference by macromolecular monomers with polyethylene crystallites. The macromolecular monomer is an alpha-olefin terminated polystyrene having a molecular weight of 27,000. The copolymer has 20% of the macromolecular monomer integrally copolymerized into the polyethylene backbone polymer. The melting behavior of the copolymer closely matches literature data for unmodified high-density polyethylene, even though the sample contains 20% of the macromolecular monomer. Undue premelting, for example, does not occur in copolymers and the melting point (T,,,) is the same for both 100% polyethylene and copolymer samples. Also, on the basis of comparable polyethylenes made without macromolecular monomers using the same polymerization, the initial lift-ofi temperature (89 C.) averaged 7 C. higher for macromolecular monomer procedures containing samples. In one sample, the temperature increase is 19 C. over the base polyethylene.

Crystallinity measurements are calculated from heat of fusion (AH) data obtained from the area under the DSC trace. The calculations are based on an AH of 68.4 cal/ g. for 100% crystalline polyethylene. Although at a different level, the crystallinity values by this method generally paralleled those obtained by X-ray.

The therma data on melting and crystallinity thus confirms the X-ray data that the integrity of the polyethylene crystallites is maintained in the copolymer of the present invention. The reverse efiect is generally observed, however, in polyethylene copolymers of the prior art or in polyethylene with sidechains simply attached to the polyethylene. Often in these instances, crystallinity not only decreases by more than a simple dilution factor, but also the polyethylene crystallites may show low values for T and AH.

Crystallite Orientation X-ray diffraction patterns were taken of stretched Instron test samples to determine crystallite orientation and the effect of macromolecular monomer addition on the ability of the crystallites to orient. The degree of orientation is determined from the size of the angle subtended by the arcs of the 110 and 200 diffraction peaks that are shown by oriented samples. Commercial high density polyethylene, unstretched and stretched (500%) were compared with a graft copolymer of a polyethylene backbone having 20% by weight incorporation of polystyrene sidechains, stretched, 800%. A stretched homopolymer shows a small 110 are that subtends an angle of 17, whereas the angle for the copolymer is 48 even though it is stretched more than the homopolymer. Hence, the macromolecular monomer phase acts within the amorphous regions to tie and hold the crystallite together at high elongations.

In molded films, on the other hand, a somewhat opposite effect is noted since copolymers show higher degrees of crystal plane orientation than homopolymers. The ratio of the 110 peak over the 200 peak height is used in these instances. When the ratio of peak intensities is in the order of 3.3, the polyethylene sample is considered to have random orientation. For homopolymer polyethylenes, we prepared and tested the 110/200 peak ratio varied from 3.0 to 4.6. The orientation ratio for copolymers varied from about 3 to as high as 7.3 for samples mounted in the diifractometer with their film surface parallel to the sample holder. Molded specimens responded in an opposite sense, however, upon subsequent heating and cooling but without the pressure used during molding. Under these circumstances, a copolymer decreased from 7.3 to 4.8 while the base polyethylene increased from 4.6 to 5.0 in orientation. Similar changes are shown in other samples. These observations on changes in orientation further illustrate differences in polyethylene properties due to the presence of marcomolecular monomers integrally copolymerized into the polyethylene backbone.

Spherulite Formation Spherulitic structures are noted by microscopic examination in several of the polyethylene or ethylene-macromolecular monomer copolymers prepared. In molded samples, large (10-30 m.) spherulites in some of the polyethylene specimens are observed to decrease in size and in optical perfection with macromolecular monomer addition. This behavior is confirmed by crystallization from solvent (Tetrahydronaphthalene) where large and individually separated spherulitic units can be observed. Polarized light is used and pictures are taken of spherulites from a homopolymer and copolymers with 6, 8 and 20% macromolecular styrene contents. The majority of the spherulites obtained from the copolymers are smaller and show more imperfections in structure than those obtained from the homopolymer. Similar effects are assumed to take place in samples where sphcrulitic structures are on the order of 1.0 to 3.0 -,u.m. in diameter but where it is difiicult to clearly distinguish changes in structure.

To demonstrate that the observed effects are a function of copolymerization, pictures were taken of crystals from THN that were obtained from physical blends with 5, 10 and 20% levels of macromolecular monomer. The spherulitic structures of the blends were unchanged from the homopolymer.

Thus, a second feature of graft copolymers of the invention is evident in that while the polyethylene crystal-- lites themselves are not impaired, the macromolecular molecules interfere with the aggregation of crystallites into larger morphological units such as spherulites. Their action fits the pattern of being in the amorphous region of the sample and interferring with crystallites aggregation but contributing as tie molecules to film strength and elongation.

The interference with spherulite formation is also postulated as contributing towards materials with improved stress-cracking and low temperature flexibility properties.

A number of graft copolymers having polyethylene backbones and polystyrene sidechains are prepared using the procedure set forth in Examples 9 and 10. Also, a number of polyethylene homopolymers are prepared in 3-9 the same manner as described for the copolymers, except for the omission of the macromolecular monomer. Chain transfer agents are not used to control molecular weight. Products obtained with continuous ethylene addition have broad molecular weight distributions, Whereas those obnot vary significantly with either molecular weight or MWD. The elongation and tensile strength increase with increasing molecular weight, whereas the modulus, heat deflection and melt index decrease with increasing molecular weight. Examples 25 and 26 have a narrower MWD 5 tained by batch polymerizations have narrow molecular and show significant increases in elongation and tensile weight distributions. strength over equivalent weight average molecular weight The graft copolymers and the homopolymers of polypolyethylene of a broader MWD. ethylene are pressed into films, whereby they are each The summation of data for the graft copolymers are subjected to tests to determine yield strength, elongation, 10 divided into two groups, those having a polydispersity tensile strength, flex modulus, and other properties herein- (P.D.) less than 10 given in Table II and a PD. greater after set forth (using methods outlined above) to demthan 10 given in Table III in order to establish a logi: onstrate the improved properties of the graft copolymers cal comparison of the properties as can be seen from the over the homopolymer of polyethylene. The results of corresponding difference in properties with polyethylene these tests are summarized in Tables IIII below. 15 homopolymers.

TABLE I.PROPERTIES OF POLYETHYLENE HOMOPOLYMERS Flexural Heat Yield Elongamodulus deflec- M lVl'w strength tion T.S.\ (p.s.i.X tion Melt X003) X003) 1 .1). (p.s.i.) (percent) (p.s.1.) 10 F.) index l GPO computer analysis (P.D.=polydispersity).

b 20 mil. sheets 2 inches/minute crosshead on Instron tester. v x x 5" bars; Heat deflection at 264 p.s.i. fiber stress.

Nora-All physical properties are on compression molded unannealed samples.

TABLE II.PROPERTIESPO Macromolecular monomer F GRAFI COPOLYMERS HAVING POLYEIHYLENE BACKBONE AND OLYSIYRENE SIDECHAINS (NARROW MWD) Yield b Elon- Flexural Heat Mn MW MwtX strength gation b T.S, b modulus v deflection Example (10 (10) RD. 9 (10 (percent) (p.s.i.) (percent) (p.s.1.) (p.s.1. 10

v GPO computer analysis (P.D.=polydispersity).

* 20 mil sheets 2 inches/minute crosshead speed on Instron tester. 9 x 36" x 5" bars; heat deflection at 264 p.s.1. fiber stress.

d Annealed.

Q Plus macromolecular monomer.

Norm-All physical properties are on compression molded unannealed samples.

TABLE III.-PROPERTIES OF GRAFT COIOLYMERS HAVING POLYETHYLENE BACKBONE AND POLY- STYRENE SIDECHAINS (BROAD MWD.)

Macromolecular monomer Molec- Flexural ular Yield Elonmodulus Heat B Mn 3 MW B weight strength gation b .S b p.s.i. deflection Example X(10 X00 RD 6 (10 3) (Percent) (p.s.1.) (percent) (p.s.1.) X10 F.) 16. 1 232 14. 4 15 2 3, 800 850 4, 300 1. 102 37. 4 603 16. 1 15 5 3, 400 850 5, 900 1. 56 19. 3 287 14. 9 15 9 3, 600 880 5, 500 1. 41 110 17. 0 230 13. 8 15 12 4, 000 920 5, 800 26. 8 353 13. 2 15 15 4, 200 720 5, 700 1. 54 123 27. 2 347 12. 7 15 17 4, 300 650 4, 500 1. 61 141 34. 1 480 14. 0 27 3 3, 500 790 7, 000 1. 49 108 23. 3 236 10. 1 27 8 3,500 650 6, 300 1.31 106 l GPC computer analysis (P.D.=polydispersity). b 20 mil. sheets 2 inches/minute crosshead speed on Instron tester. M, x x 5 bars; Heat deflection at 264 p.s.i. fiber stress.

Norm-All physical properties are on compression molded unannealed samples.

By comparing the various properties of the graft copolymers with the homopolymers of the same average molecular weight, it is clear that the incorporation of the macromolecular monomer in the backbone of hydrocarbon polymers, such as polyethylene, improves many of the properties of polymer significantly without a sacrifice of beneficial properties possessed by the homopolymer. Such an improvement in properties is not expected in view of the fact that the macromolecular monomer is actually copolymerized into the backbone of polyethylene and in- 

1. A POLYMERIZABLE DIBLOCK MACROMOLECULAR MONOMER OF THE FORMULA: A-B-X WHEREIN A IS A POLYMERIZED MONOALKENYL SUBSTITUTED AROMATIC HYDROCARBON, B IS A POLYMERIZED CONJUGATED DIENE, AND X IS A POLYMERIZABLE END GROUP CONTAINING EITHER A VINYL MOIETY, A VINYLENE MOIETY OR AN EPOXY MOIETY, SAID DIBLOCK MACROMOLECULAR MONOMER HAVING A MOLECULAR WEIGHT IN THE RANGE OF FROM ABOUT 5,000 TO ABOUT 150,000 AND HAVING A SUBSTANTIALLY UNIFORM MOLECULAR WEIGHT DISTRIBUTION SUCH THAT ITS RATIO OF MW/MN IS LESS THAN ABOUT 1.1, SAID DIBLOCK MACROMOLECULAR MONOMER BEING FURTHER CHARACTERIZED AS HAVING NO MORE THAN ONE VINYL MOIETY, VINYLENE MOIETY OR EPOXY MOIETY ON THE TERMINAL PORTION PER LINEAR COPOLYMER CHAIN. 